Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | 13.8 MPa | 2000 psi | ASTM D412 |
S&E Specialty Polymers TufFlex™ GTPE-2272SG-K8 TPE Compound Application: A flame retardant, matte finish, 90°C oil resistant, flexible TPE jacketing material.Information provided by S&E Specialty Polymers |
|||
Tensile Strength | >= 13.8 MPa | >= 2000 psi | ASTM D638 |
S&E Specialty Polymers TufFlex™ GTPO8290 Natural TPO Compound Application: An olefin based insulation & jacketing , 105°C rated compound formulated with excellent deformation characteristics. (SEW, SJEW)Information provided by S&E Specialty Polymers |
|||
Tensile Strength | 13.8 MPa | 2000 psi | ASTM D412 |
S&E Specialty Polymers TufTech™ GA-1038 Natural MA PVC Compound Application: A RoHS compliant, 60°C PVC wire and cable compound. Material is suitable for 60°C and 75°C SVT and SJT insulation.Information provided by S&E Specialty Polymers |
|||
Tensile Strength | 13.8 MPa @Strain 100 % |
2000 psi @Strain 100 % |
510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Flexible B4D01 Polyvinyl Chloride, Flexible (PVC, Flexible) Information provided by PolyOne |
|||
Tensile Strength | 13.8 MPa | 2000 psi | across grain; ASTM F152 |
Garlock 2930 Compressed Aramid Fiber Gasketing, Neoprene Binder Aramid fibers with a Neoprene binder.Ideal for utility servicesExcellent sealabilityImproved thermal stabilityGood for general serviceMedia: Water, steam, refrigerants, oils, fuels, mild acids, and.. |
|||
Tensile Strength | 13.8 MPa | 2000 psi | Typical |
Garlock 361 Nitrile Sheet Rubber Nitrile sheet is primarily used for applications where resistance to oil, solvents and fuels is required.Style #361 has a higher tensile strength and is a superior product in applications requiring .. |
|||
Tensile Strength | 13.8 MPa | 2000 psi | Typical |
Garlock 5360 Nitrile Sheet Rubber Nitrile sheet is primarily used for applications where resistance to oil, solvents and fuels is required.Style #5360 is a medium-hard, premium-grade nitrile sheet, also available in 40, 50, 70 and 8.. |
|||
Tensile Strength | >= 13.8 MPa | >= 2000 psi | |
Garlock 7164 SBR Rubber Lining SBR rubber lining for protection applications such as chute lining and skirtboards.An optional duck fabric backing is available.Information provided by Garlock Rubber Technologies |
|||
Tensile Strength | >= 13.8 MPa | >= 2000 psi | |
Garlock 7986 Neoprene Sheet Rubber This blended neoprene sheet is used where good oil, petroleum, ozone and weathering-resistance is needed.Black, smooth cloth finishInformation provided by Garlock Rubber Technologies |
|||
Tensile Strength | 13.8 MPa | 2000 psi | across grain; ASTM F152 |
Garlock GYLON® 3502 PTFE Gasketing, Silica Filler, Oxygen Service PTFE with silica filler - Oxygen serviceImproved sealing performance over conventional PTFEUnique manufacturing process minimizes cold flow problems typical of skived and expanded PTFE sheetsExcelle.. |
|||
Tensile Strength | 13.8 MPa | 2000 psi | across grain; ASTM F152 |
Garlock GYLON® 3503 PTFE Gasketing, Barium Sulfate Filler, Oxygen Service PTFE with barium sulfate filler - Oxygen service.Improved sealing performance over conventional PTFEUnique manufacturing process minimizes cold flow problems typical of skived and expanded PTFE shee.. |
|||
Tensile Strength | >= 13.8 MPa | >= 2010 psi | NBR NM-IEC 60811-1-1 |
Karina E 105852-35/1-A-IS-L Ivory PVC Compound PVC compound recommended for extrusion of wires THHN and THWN.Information provided by Karina Indústria e Comércio de Plásticos Ltda. |
|||
Tensile Strength | 13.8 MPa | 2000 psi | |
Garlock 681 Vegetable Fiber Gasketing Vegetable fiber with glue-glycerin binder (branded).Style 681 is designed for use in lightweight flanges and is compatible with water and most hydrocarbons.Information provided by Garlock Rubber Tec.. |
|||
Tensile Strength | 13.8 MPa | 2000 psi | ASTM F152 |
Garlock 9122 Nitrile Sheet Rubber Gasketing Nitrile (NBR)Superior resistance to aliphatic hydrocarbons, such as oil, fuels, and many types of solvents.Information provided by Garlock Rubber Technologies |
|||
Tensile Strength | 13.8 MPa | 2000 psi | ASTM D412 |
Garlock 9200 Nitrile Rubber Gasketing, Nylon Insert Nitrile rubber with proprietary nylon insertCombines elasticity and extensibility of rubber with strength of fabric insert. Specially compounded in varying burst strengths for almost any service co.. |
|||
Tensile Strength | 13.8 MPa | 2000 psi | ASTM D1708 |
Saint-Gobain Fluoroloy® A12 High Performance Seal Material Excellent wear and heat resistance; Non-abrasive; Recommended for moderate to high speed service running against soft or hard metals; Performs well against lubricated and non-lubricated surfacesInfo.. |
|||
Tensile Strength | 13.8 MPa | 2000 psi | ASTM D638 |
Saint-Gobain Rulon® 488 Grade Bearing/Seal PTFE Description: Rulon® is the Saint-Gobain trade name for their family of proprietary PTFE compounds. This family of materials offers the combination of high compressive strength, low coefficient of.. |
|||
Tensile Strength | 13.8 MPa | 2000 psi | ASTM D638 |
Saint-Gobain Rulon® 641 Grade Bearing/Seal PTFE Description: Rulon® is the Saint-Gobain trade name for their family of proprietary PTFE compounds. This family of materials offers the combination of high compressive strength, low coefficient of.. |
|||
Tensile Strength | 13.8 MPa | 2000 psi | ASTM D638 |
Techmer ES Plastiblend® PA6 GF20 RM BK Nylon 6 Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber ReinforcementProcessing Method: Injection MoldingInformation provided by TP Composites, Inc. |
|||
Tensile Strength | 13.8 MPa | 2000 psi | ASTM D638 |
Saint-Gobain Rulon® AR Bearing/Seal PTFE Rulon® AR is somewhat more flexible than Rulon® LR, hence suitable for seals and bonded coating of slide surfaces. It has many decades of use in automotive shaft seals and fuel metering pump c.. |
|||
Tensile Strength | 13.8 MPa | 2000 psi | NBR Conductive Hose Compound |
TIMCAL ENSACO™ 250G Conductive Carbon Black ENSACO™ & SUPER P™ conductive carbon blacks are carbon blacks with a high to very high void volume allowing the retention of a carbon network at low to very low filler content. The void volume can.. |
|||
Tensile Strength | 13.8 MPa | 2000 psi | ASTM D412 |
Lubrizol ESTANE® 58244 Ether Based Thermoplastic Polyurethane Features: Non-Halogenated flame retardant compoundUses: Extrusion – wire and cable and general extrusion where flame retardant propertied are requiredAvailable in Americas, Europe, Middle East, Afr.. |
|||
Tensile Strength | 13.8 MPa | 2000 psi | |
AlphaGary Garaflex™ E 4762 A1 LCF Vinyl Thermoplastic Elastomer Garaflex™ E is a vinyl based thermoplastic elastomer used mostly in wire and cable105°C rated low temperature flexible booster cable jacket application |
|||
Tensile Strength | 13.8 MPa | 2000 psi | |
AlphaGary Garaflex™ E 4762-A5 LCF Vinyl Thermoplastic Elastomer Garaflex™ E is a vinyl based thermoplastic elastomer used mostly in wire and cable105°C rated flexible jacket / insulation compound with excellent low temperature properties |
|||
Tensile Strength | 13.8 MPa | 2000 psi | |
AlphaGary PVC GM 8015-O Natural LCF Polyvinyl Chloride Thermoplastic A lead / cadmium free, 105°C, UL-94 V-O rated, electrical grade molding compound |
|||
Tensile Strength | 13.8 MPa | 2000 psi | |
AlphaGary Garaflex™ O 9940 SA Olefinic Thermoplastic Elastomer Garaflex™ O is a flame retarded, olefinic thermoplastic elastomer105°C rated flame retardant olefinic TPE for flat ribbon cable and heat tracing cable |
|||
Tensile Strength | 13.8 MPa | 2000 psi | across grain; ASTM F152 |
Garlock GYLON® 3505 PTFE Gasketing, Glass Microsphere Filled PTFE with aluminosilicate microspheres - NSF 61 approved (drinking water) - Oxygen serviceImproved sealing performance over conventional PTFEUnique manufacturing process minimizes cold flow problems.. |
|||
Tensile Strength | 13.8 MPa @Strain 100 % |
2000 psi @Strain 100 % |
Type IV, 510 mm/min; ASTM D638 |
PolyOne Geon™ Vinyl Wire & Cable W649LF Polyvinyl Chloride, Flexible (PVC, Flexible) Typical Properties of Molded Slab (0.075); Not to be Construed as Specifications. Provisional Product Information - Physical and Mechanical properties based on initial production.Information provide.. |