- Polymer Property : Melt Flow = 7.5 g/10 min
Polymer Property : Melt Flow = 7.5 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
7.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| PolyOne Maxxam™ FR WC-P85 NHFR RoHS Natural Polyolefin, Unspecified Maxxam™ HFFR WC-P85 RoHS Natural is a halogen-free flame retardant polyolefin compound characterized by low smoke, low flame spread, excellent spring-back, no plate-out and high extrusion line spee.. |
|||
| Melt Flow | 7.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
7.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
| Polimeri Europa Edistir RT 441M Polystyrene High impact polystyrene combining high toughness and high stiffness with good flowability for easy processing. Designed for injection moulding of technical parts, housings and covers.
Especially rec.. |
|||
| Melt Flow | 7.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| SABIC Innovative Plastics Lexan® 500R PC 10% GR PC. Optimum combination of high modulus plus excellent impact strength and flame retardance. Internal mold release. |
|||
| Melt Flow | 7.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| SABIC Innovative Plastics Lexan® LUX1619 PC Lexan* LUX1619 Polycarbonate resin is an extrusion grade. It is UL94 HB rated. It was designed for high light reflectance. |
|||
| Melt Flow | 7.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| SABIC Innovative Plastics Lexan® OQ2720 PC Ophthalmic/safety lens market. OQ2xxx series in all transparent tints. Dedicated equipment, stringent production control conditions. |
|||
| Melt Flow | 7.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
7.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| Network Polymers 702 Polystyrene Description: Ignition RetardantInformation provided by Network Polymers Inc. |
|||
| Melt Flow | 7.5 g/10 min @Load 5.00 kg, Temperature 190 °C |
7.5 g/10 min @Load 11.0 lb, Temperature 374 °F |
|
| Total Finaprene® 507 Styrene-Butadiene TPE Copolymer
(discontinued **) Styrene-Butadiene CopolymerDescription: Finaprene® 507 is a thermoplastic elastomer type radial styrene-butadiene block copolymer. Thanks to its high styrene content, Finaprene® 507 provides exce.. |
|||
| Melt Flow | 7.5 g/10 min | 7.5 g/10 min | Condition G |
| Ineos Nova 2511 General Purpose Crystal Polystyrene
(discontinued **) High speed molding, Improved crack resistance, USP Class VIApplications: Cutlery, Light louvers, RazorsExposure to gamma radiation in the 2.02-6.06 megarad range has no significant effect on the phy.. |
|||
| Melt Flow | 7.5 g/10 min @Load 2.16 kg, Temperature 330 °C |
7.5 g/10 min @Load 4.76 lb, Temperature 626 °F |
cm³/10 min. |
| Covestro Apec® DP 1-9379/7 Polycarbonate
(discontinued **) Key Features:Release agentUnfilledU.V. stabilized or stable to weatherSuitable processing methods:Injection moldingThermoformingInformation provided by Bayer Polymers.As of 1 September 2015, Bayer M.. |
|||
| Melt Flow | 7.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
7.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Chevron Phillips K-Resin® KR10 Styrene-Butadiene Copolymer, Film Grade
(discontinued **) Styrene-Butadiene Copolymer. Properties below based on 1 mil ( 0.025 mm) film; 2.5:1 Blow Up Ratio; 35 mil (0.90 mm) die gap.Customer Benefits: This SBC is easily processed on blown film or cast fi.. |
|||
| Melt Flow | 7.5 g/10 min | 7.5 g/10 min | ASTM D1238 |
| Kolon DIAMAT® IM Description: DIAMAT® is a specially formulated high impact grade PMMA resin from KOLON. The acrylic composition results in an excellent balance of impact resistance and high modulus at reasonabl.. |
|||
| Melt Flow | 7.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
7.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM-D1238 |
| Ineos ABS Lustran® SAN DN79 SAN Grade Lustran® SAN DN79 is a natural color, styrene-acrylonitrile copolymer supplied in pellet form. It is designed for used in compounding. |
|||
| Melt Flow | 7.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
Calculated from Volume Flow Rate of 6 cm<sup>3</sup>/10min.; ISO 1133 |
| Mitsubishi Xantar® G2F 23 UR Polycarbonate-10% Glass Reinforced Xantar® materials are engineered for performance, consistency and reliability. This makes Xantar® resins ideal for interior automotive components, electrical equipment and consumer appliances .. |
|||
| Melt Flow | 7.5 g/10 min @Load 6.60 kg, Temperature 337 °C |
7.5 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| SABIC Innovative Plastics ULTEM AUR200G6 PEI (Europe-Africa-Middle East) The data listed in this data sheet are the lower specification limits, apart from the MFR, CTE, HDT at 1.8 MPa, Density, Tensile strain, Water Absorption, Thermal Conductivity and Shrinkage which ar.. |
|||
| Melt Flow | 7.5 g/10 min @Load 10.0 kg, Temperature 220 °C |
7.5 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Samsung Cheil Industries Starex® SL-0110 ABS, Unreinforced Information provided by Samsung Cheil Industries. |
|||
| Melt Flow | 7.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
7.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Supreme Petrochem SH 825 High Impact Polystyrene Characteristics Good flow properties Very good stiffness High heat grade Processing MoldingApplications Home appliances, lamp shades, wall clocks Gift sets, picnic boxes Air cooler, watch casesM.. |
|||
| Melt Flow | 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
7.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| SCG Chemicals EL-Leneâ„¢ H6007JU High Density Polyethylene Injection Molding Key Characteristics:Good processabilityHigh rigidityHigh impact resistanceGood weathering resistance (UV stabilizer)Recommended Applications:Crates for soft drink, bottles, pallet, garbage bins, con.. |
|||
| Melt Flow | 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
7.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Borealis MA8200 Polyethylene Information provided by Borealis AG |
|||
| Melt Flow | 7.5 g/10 min @Load 10.0 kg, Temperature 230 °C |
7.5 g/10 min @Load 22.0 lb, Temperature 446 °F |
ISO 1133 |
| Polyram RamClean™ 800 Ethylene Propylene Compound Purging Agent Ethylene propylene compound purging agent for extruders/injection molding machines.Information provided by Polyram. |
|||
| Melt Flow | 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
7.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Total LDPE LA 0710 Low Density Polyethylene - Extrusion Coating LDPE LA 0710 is a low density polyethylene made by a high pressure autoclave process without antioxidant.Application examples: coating of paper, paperboard, aluminum. High draw down, low neck in.In.. |
|||
| Melt Flow | 7.5 g/10 min | 7.5 g/10 min | Condition G; ASTM D1238 |
| Chevron Phillips K-Resin® DK11 Styrene-Butadiene Copolymer, Film Grade Styrene-Butadiene Copolymer. Properties below based on 1 mil ( 0.025 mm) film; 2.5:1 Blow Up Ratio; 35 mil (0.90 mm) die gap.Customer Benefits: Provides the same high performance film properties as.. |
|||
| Melt Flow | 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
7.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| ExxonMobil LDPE LD 200.48 Low Density Polyethylene Resin Product Description: LD 200.48 is a general purpose LDPE extrusion coating grade, designed for flexible packaging applications. It offers – Low neck-in – Very good adhesion – Excellent heat seala.. |
|||
| Melt Flow | 7.5 g/10 min @Load 2.16 kg |
7.5 g/10 min @Load 4.76 lb |
|
| Dow AFFINITY™ PT 1450 Polyolefin Plastomer AFFINITY® PT 1450 polyolefin plastomer for extrusion coated packaging is an ethylene alpha olefin resin for monolayer and coextrusion coating that offers excellent low temperature seal initiation, .. |
|||
| Melt Flow | 7.5 g/10 min @Load 2.16 kg, Temperature 230 °C |
7.5 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Braskem BC 818 LDPE Extrusion Coating Polyethylene 38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Extrusion coating. Information provided by Braskem |
|||
| Melt Flow | 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
7.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Barlog Plastics KEBAFORM C 901 TF POM Copolymer unreinforced, improved wear and friction POMInformation provided by BARLOG plastics GmbH. |
|||
| Melt Flow | 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
7.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| BASF Ultraform N 2320 U03 UNC Q600 POM Ultraform N2320 U03 UNC Q600 is a rapidly freezing UV stabilized general-purpose injection molding grade. |
|||
| Melt Flow | 7.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
7.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
DIN 5375/ISO 1133 |
| Ineos Nova S-4122 Medium Impact Compact Polystyrene
(discontinued **) Low friction, medium impact polystyrene which combines excellent flow characteristics with a good dimensional stability under heat and a high stiffness. This grade is designed for injection moldin.. |
|||
| Melt Flow | 7.5 g/10 min | 7.5 g/10 min | Condition G; ASTM D1238 |
| Chevron Phillips K-Resin® BK18 Styrene-Butadiene Copolymer
(discontinued **) Characteristics: Good flexibilityGood impact resistanceGood clarityGood mold releaseApplications: ToysOvercapsConsumer productsInformation provided by Chevron Phillips. |
|||