Polymer Property : Melt Flow = 0.90 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Flow	0.90 g/10 min @Load 2.16 kg, Temperature 190 °C	0.90 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
NOVA Chemicals Novapol® TD-9022-C Superhexene LLDPE Puncture value is 60 J/mm. Additive Package: Antiblock.Applications: industrial liners, heavy duty packaging.Film properties are typical of 25 µm blown film extruded at a blow-up ratio of 2.5:1, b..
Melt Flow	0.90 g/10 min @Load 3.80 kg, Temperature 230 °C	0.90 g/10 min @Load 8.38 lb, Temperature 446 °F
Polycasa Acryl® G 88 E Acrylic Same as Lucryl G 88, but higher resistance to stress cracking and higher processing viscosity. Used for: extruded protective layer on PVC, ABS and PC for outdoor applications, as well as bath tubs ..
Melt Flow	0.90 g/10 min	0.90 g/10 min	ASTM D1238E
Chevron Phillips MarFlex® 7109S LLDPE Blown Film Resin (discontinued **) Resin Type: linear low density polyethylene, hexene copolymerCharacteristics: good stiffness at thin gauges, good drawdown, excellent processability, can use straight or in blends with LDPE or HDPE,..
Melt Flow	0.90 g/10 min	0.90 g/10 min	Condition E; ASTM D 1238
Chevron Phillips 7109LT LLDPE Blown Film Resin, Hexene Copolymer (discontinued **) Resin Type: Hexene Copolymer, High Antiblock Version of 7109TCharacteristics: Good Stiffness at Thin Gauges, Good Drawdown, Low COF, Can be used straight or blended with LDPE or HDPEApplications:Ind..
Melt Flow	0.90 g/10 min	0.90 g/10 min	ASTM D1238
Chevron Phillips 7109D Linear low density polyethylene blown film resin (discontinued **) Resin Type: linear low density polyethylene, hexene copolymer, no slip, no antiblock version of 7109 with process aid, cast/blown resinCharacteristics: good stiffness at thin gauges, good drawdown, ..
Melt Flow	0.90 g/10 min	0.90 g/10 min	ASTM D1238
Chevron Phillips 6109FK Linear low density polyethylene blown film resin (discontinued **) Resin Type: linear low density polyethylene, butene copolymer, medium antiblock, medium slip, process aid version of 6109, blown film resinCharacteristics: good stiffness at thin gauges, good drawdo..
Melt Flow	0.90 g/10 min @Load 2.16 kg, Temperature 190 °C	0.90 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
M. Holland Company LL104 LLDPE (discontinued **) Additives: Antiblock, SlipFeatures: Unspecified Antiblocking, Butene Comonomer, Copolymer, Good Drawdown, Good Processability, Unspecified SlipUses: Film, LinersApprovals: FDA 21 CFR 177.1520(c) 2.2..
Melt Flow	0.90 g/10 min @Load 2.16 kg, Temperature 230 °C	0.90 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
NOVA Chemicals DYLARK® 250 Impact Grade Engineering Resin Features:High heat resistance Good chemical resistance High impact strength Excellent flow characteristicsApplications:Automotive interior trim applications Automotive consoles Structural HousingsIn..
Melt Flow	0.90 g/10 min	0.90 g/10 min	Exxon Method
ExxonMobil Escorene® LD-333 EVA Film Resin, Very High Clarity, Very High Impact (discontinued **) Data provided by the manufacturer, Exxon Chemical.A 9.0% vinyl acetate copolymer film resin. Film made from LD-333 exhibits superior impact strength, clarity and heat sealability.Applications: Prim..
Melt Flow	0.90 g/10 min @Load 2.16 kg	0.90 g/10 min @Load 4.76 lb	ASTM D1238
Reliance Industries Reclair F19010 Polyethylene Blow film Linear Low Density Polyethylene grade. Reclair F19010 is butene comonomer based, with optimum levels of antioxidants, antiblocking agents, slip additives, and polymer processing aids. Th..
Melt Flow	0.90 g/10 min @Load 2.16 kg, Temperature 190 °C	0.90 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
DuPont™ Surlyn® 1855 Zinc Ionomer Resin for Blown and Cast Film (discontinued **) Surlyn® 1855 is an ionomer resin available for use in conventional blown and cast film extrusion and coextrusion equipment designed to process polyethylene resins. Applications: Meat, poultry, sea..
Melt Flow	0.90 g/10 min @Load 2.16 kg, Temperature 230 Â°C	0.90 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ISO 1133
Inno-Comp INNOPOLÂ® CS 2-8960 60% Barium-Sulfate Filled Polypropylene Block-Copolymer INNOPOLÂ® CS 2-8960 is a 60% Barium-sulfate filled compound based on polypropylene block-copolymer. This grade is available in nature and custom colored form.INNOPOLÂ® CS 2-8960 is developed for..
Melt Flow	0.90 g/10 min	0.90 g/10 min	ISO 1133
Lucite International DiakonÂ® TD542 Toughened Acrylic Compound The DiakonÂ® impact PMMA series offer the best combination of impact, chemical and heat resistance and provide rigidity and surface hardness.The grades in the DiakonÂ® series can be processed by..
Melt Flow	0.90 g/10 min @Load 2.16 kg	0.90 g/10 min @Load 4.76 lb	ISO 1133
SIDPEC EGYPTENEÂ® LL 0209 KJ LLDPE Film Applications:Refuse sacksProduce bags, carrier bagsFilm properties were measured on 38 micron film extruded at a blow up ratio of 2:1.Information provided by Interchim s.r.l., official distributor o..
Melt Flow	0.90 g/10 min @Load 2.16 kg, Temperature 230 °C	0.90 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Borealis BB108E Polypropylene compound for Steel Pipe Coating BB108E is a high molecular weight, low melt flow rate polypropylene block copolymer. Applications: BB108E is recommended for steel pipe coating.Information provided by Borealis AG
Melt Flow	0.90 g/10 min @Load 2.16 kg, Temperature 230 °C	0.90 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
Borealis Borcoat™ BB108E-1199 White Polypropylene Block Copolymer for Steel Pipe Coating Borcoat BB108E-1199, a ready made white compound, is a highly molecular weight, low melt flow polypropylene block copolymer. As a top-coat in three component polypropylene systems, Borcoat BB108E-1..
Melt Flow	0.90 g/10 min	0.90 g/10 min	LE 4421; ASTM D1238
Borealis Visico™ LE4423/LE4432 Scorch Retardant, Moisture-Crosslinking Polyethylene Compound for Low Voltage Installation Visico LE4423/LE4432 is a black, moisture-induced crosslinking polyethylene compound that is designed for use as low voltage wire insulation and jacketing. The combination of a Visico base material..
Melt Flow	0.90 g/10 min	0.90 g/10 min	ASTM D1238
A. Schulman POLYFLAM™ CFP 4611 11% CACO3 filled copolymer polypropylene product DescriptionPolyfort® CFP 4611 is an 11% CACO3 filled copolymer polypropylene product. Information provided by A. Schulman.
Melt Flow	0.90 g/10 min @Load 5.00 kg, Temperature 190 °C	0.90 g/10 min @Load 11.0 lb, Temperature 374 °F	ISO 1133/T
Total MDPE 3802 YCF Medium Density Polyethylene, Pipes & Fittings MDPE 3802 YCF is a high performance hexene-based yellow compound, with a MRS 8 MPa - PE 80 classification, and primarily intended for gas pipe applications.MDPE 3802 YCF key characteristics are a su..
Melt Flow	0.90 g/10 min @Load 5.00 kg, Temperature 190 °C	0.90 g/10 min @Load 11.0 lb, Temperature 374 °F	ISO 1133/T
Total MDPE LF 38 YS CF Medium Density Polyethylene, Stripes MDPE LF 38 YSCF is a yellow stripe compound designed to be used in combination with the black PE 80 grade MDPE 3802 B for gas networks.An accredited laboratory has proved fusion compatibility of the..
Melt Flow	0.90 g/10 min @Load 5.00 kg	0.90 g/10 min @Load 11.0 lb	ISO 1133
Total LF 38 YS CF MDPE, pipe FINATHENE® LF 38 YS CF is a cadmium-free yellow stripe compound designed to be used in combination with FINATHENE® 3802 B for gas pipe application. The base polymer of FINATHENE® LF 38 YS CF is t..
Melt Flow	0.90 g/10 min @Load 2.16 kg, Temperature 190 °C	0.90 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133/D
Total Lumicene® mPE M 3509 Medium Density Polyethylene, Blow Molding Lumicene® mPE M 3509 is a metallocene-based medium density polyethylene combining the features of conventional blow molding polyethylene with differentiated optical propertied such as gloss and co..
Melt Flow	0.90 g/10 min @Temperature 230 °C	0.90 g/10 min @Temperature 446 °F	Condition L; ASTM D1238
A. Schulman POLYFORT™ FPP 1182E Talc Filled, Extrusion Grade Copolymer Polypropylene DescriptionPolyfort® FPP 1182E is a 20% talc-filled, extrusion grade copolymer polypropylene. It had a good balance of flexural modulus, low temperature impact, and appearance properties. Informat..
Melt Flow	0.90 g/10 min	0.90 g/10 min	ASTM D1238E
Chevron Phillips MarFlex® 7109 LLDPE Blown Film Resin Resin Type: linear low density polyethylene, hexene copolymerCharacteristics: good stiffness at thin gauges, good drawdown, excellent processability, can use straight or in blends with LDPE or HDPE,..
Melt Flow	0.90 g/10 min	0.90 g/10 min	ASTM D1238E
Chevron Phillips MarFlex® 7109DJ LLDPE Blown Film Resin Resin Type: linear low density polyethylene, hexene copolymerCharacteristics: good stiffness at thin gauges, good drawdown, excellent processability, can use straight or in blends with LDPE or HDPE,..
Melt Flow	0.90 g/10 min	0.90 g/10 min	Condition 190/2.16; ASTM D1238
Chevron Phillips MarFlex® D139 m-LLDPE Linear Low Density Polyethylene Low Density PolyethyleneCustomer Benefits: Possesses the typical physical properties of metallocene polyethylenes with the added potential benefit of improved processability (bubble stability, down-..
Melt Flow	0.90 g/10 min @Load 2.16 kg, Temperature 190 °C	0.90 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
M. Holland Company LL106 LLDPE (discontinued **) Additives: Antiblock, SlipFeatures: Unspecified Antiblocking, Hexane Comonomer, Copolymer, Good Drawdown, Good Processability, Unspecified SlipUses: Film, LinersApprovals: FDA 21 CFR 177.1520(c) 2.2..
Melt Flow	0.90 g/10 min @Load 2.16 kg, Temperature 230 °C	0.90 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
E-Polymers EFLEX® S5060 Extrusion S-series ( SBS, SEBS compound resins): E-FLEX S series resins are based on SBS/SEBS/SEEPS/PP exhibiting excellent high and low temperature resistance and easy processing with conventional thermoplas..
Melt Flow	0.90 g/10 min	0.90 g/10 min	Condition L; ASTM D1238
Asahi Kasei Delpet® 80N Acrylic Molding Compound, High Heat Grade 80N has high heat resistance and strength. Recommended for taillight lenses, reflectors, and other auto parts, and general lighting fixtures. General Delpet® qualities include attractive transpar..
Melt Flow	0.90 g/10 min @Load 5.00 kg, Temperature 190 °C	0.90 g/10 min @Load 11.0 lb, Temperature 374 °F	ISO 1133
Borealis Borstar® ME3444 Blue Medium Density Polyethylene for Drinking Water Pipes Borstar 3444 is a blue, bimodal, medium density polyethylene classified as a MRS 8.0 material (PE80) produced with the advanced Borstar technology. A combination of pigments and stabilizers is incl..