Polymer Property : Melt Index of Compound = 8.0 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Index of Compound	5.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C	5.0 - 8.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Petroquimica Triunfo Trithene® JX 7065 LDPE - Injection Molding and Master Batch The Trithene® JX 7065 resin is a low-density polyethylene with a wide molecular weight distribution, developed to offer good impact resistance, excellent flexibility, and high resistance to stress ..
Melt Index of Compound	4.1 - 8.0 g/10 min	4.1 - 8.0 g/10 min
Sibur 21060 Polypropylene Compounding for stabilization 16K, 16V, 16N, 16M, 16H superior quality. For production of technical and domestic products of complicated profile, of non-woven materials.
Melt Index of Compound	6.0 - 8.0 g/10 min	6.0 - 8.0 g/10 min	2.16/190; ASTM D1238
A. Schulman POLYAXIS® LPA815 LPA 815EVA DescriptionPolyaxis LPA 815 is an EVA which is soft an pliable, even at low temperatures.NOTE: Physical properties are based on rotationally molded samples from unpigmented resin. Density and ESCR ..
Melt Index of Compound	4.0 - 8.0 g/10 min	4.0 - 8.0 g/10 min	ASTM D1238
A. Schulman POLYFORT™ FPP 4020 20% Mineral-Filled Polypropylene DescriptionPolyfort® FPP 4020 is a 20% mineral-filled polypropylene designed for use when improved heat resistance and high stiffness is needed.Information provided by A. Schulman.
Melt Index of Compound	6.0 - 8.0 g/10 min	6.0 - 8.0 g/10 min	2.16/190; ASTM D1238
A. Schulman POLYAXIS® LPA815 LPA 815EVA DescriptionPolyaxis LPA 815 is an EVA which is soft an pliable, even at low temperatures.NOTE: Physical properties are based on rotationally molded samples from unpigmented resin. Density and ESCR ..
Melt Index of Compound	4.0 - 8.0 g/10 min	4.0 - 8.0 g/10 min	ASTM D1238
A. Schulman POLYFORT™ FPP 4020 20% Mineral-Filled Polypropylene DescriptionPolyfort® FPP 4020 is a 20% mineral-filled polypropylene designed for use when improved heat resistance and high stiffness is needed.Information provided by A. Schulman.
Melt Index of Compound	6.0 - 8.0 g/10 min	6.0 - 8.0 g/10 min	2.16/190; ASTM D1238
A. Schulman POLYAXIS® LPA815 LPA 815EVA DescriptionPolyaxis LPA 815 is an EVA which is soft an pliable, even at low temperatures.NOTE: Physical properties are based on rotationally molded samples from unpigmented resin. Density and ESCR ..
Melt Index of Compound	4.0 - 8.0 g/10 min	4.0 - 8.0 g/10 min	ASTM D1238
A. Schulman POLYFORT™ FPP 4020 20% Mineral-Filled Polypropylene DescriptionPolyfort® FPP 4020 is a 20% mineral-filled polypropylene designed for use when improved heat resistance and high stiffness is needed.Information provided by A. Schulman.
Melt Index of Compound	6.0 - 8.0 g/10 min	6.0 - 8.0 g/10 min	2.16/190; ASTM D1238
A. Schulman POLYAXIS® LPA815 LPA 815EVA DescriptionPolyaxis LPA 815 is an EVA which is soft an pliable, even at low temperatures.NOTE: Physical properties are based on rotationally molded samples from unpigmented resin. Density and ESCR ..
Melt Index of Compound	4.0 - 8.0 g/10 min	4.0 - 8.0 g/10 min	ASTM D1238
A. Schulman POLYFORT™ FPP 4020 20% Mineral-Filled Polypropylene DescriptionPolyfort® FPP 4020 is a 20% mineral-filled polypropylene designed for use when improved heat resistance and high stiffness is needed.Information provided by A. Schulman.
Melt Index of Compound	4.0 - 8.0 g/10 min	4.0 - 8.0 g/10 min	ASTM D1238
A. Schulman POLYFORT™ FPP 4020 20% Mineral-Filled Polypropylene DescriptionPolyfort® FPP 4020 is a 20% mineral-filled polypropylene designed for use when improved heat resistance and high stiffness is needed.Information provided by A. Schulman.
Melt Index of Compound	4.0 - 8.0 g/10 min	4.0 - 8.0 g/10 min	ASTM D1238
A. Schulman POLYFORT™ FPP 4020 20% Mineral-Filled Polypropylene DescriptionPolyfort® FPP 4020 is a 20% mineral-filled polypropylene designed for use when improved heat resistance and high stiffness is needed.Information provided by A. Schulman.
Melt Index of Compound	6.0 - 8.0 g/10 min	6.0 - 8.0 g/10 min	2.16/190; ASTM D1238
A. Schulman POLYAXIS® LPA815 LPA 815EVA DescriptionPolyaxis LPA 815 is an EVA which is soft an pliable, even at low temperatures.NOTE: Physical properties are based on rotationally molded samples from unpigmented resin. Density and ESCR ..
Melt Index of Compound	6.0 - 8.0 g/10 min	6.0 - 8.0 g/10 min	2.16/190; ASTM D1238
A. Schulman POLYAXIS® LPA815 LPA 815EVA DescriptionPolyaxis LPA 815 is an EVA which is soft an pliable, even at low temperatures.NOTE: Physical properties are based on rotationally molded samples from unpigmented resin. Density and ESCR ..
Melt Index of Compound	5.0 - 8.0 g/10 min	5.0 - 8.0 g/10 min	ASTM D1238
Cheng Yu Plastic VH823 Flame Retardant ABS, High Impact
Melt Index of Compound	5.0 - 8.0 g/10 min	5.0 - 8.0 g/10 min	ASTM D1238
Cheng Yu Plastic VH825 Flame Retardant ABS, Medium Impact
Melt Index of Compound	5.0 - 8.0 g/10 min	5.0 - 8.0 g/10 min	ASTM D1238
Cheng Yu Plastic VH826 Flame Retardant ABS, Medium Impact
Melt Index of Compound	6.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C	6.0 - 8.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Arkema Group LOTRYL® 28 MA 07 Copolymer Ethylene - Methyl Acrylate LOTRYL® 28 MA 07 is a random copolymer of ethylene and methyl acrylate made by high-pressure radicalar polymerisation process. Due to the high methyl acrylate content, LOTRYL® 28 MA 07 is a polyme..
Melt Index of Compound	6.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C	6.0 - 8.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Arkema Group OREVAC® 9318 EVA Terpolymer OREVAC® is a range of ethylene-vinyl acetate copolymers modified by adjunction of polar groups which, when molten, have excellent adhesive properties to various substrates. They are supplied as fre..
Melt Index of Compound	6.0 - 8.0 g/10 min	6.0 - 8.0 g/10 min	ASTM D1238
Cheng Yu Plastic IPS610BK Electric Conducting HIPS, Extrusion
Melt Index of Compound	5.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C	5.0 - 8.0 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Arkema Group EVATANE® 28-05 Copolymer Ethylene - Vinyl Acetate EVATANE® 28-05 is a random copolymer of Ethylene and Vinyl Acetate made by high-pressure radicalar polymerisation process. EVATANE® 28-05 is stabilized with antioxidants. The High Vinyl Acetate co..