Physical Properties | Metric | English | Comments |
---|---|---|---|
Particle Size | 106 - 212 µm | 106 - 212 µm | Range |
Potters Industries Spheriglass® 2024 Solid Glass Spheres Description: Spheriglass® fine solid glass spheres are used as an additive for thermoplastic and thermosetting resin systems. Glass spheres give products many benefits such as:Low Uniform Shrinkage.. |
|||
Particle Size | <= 106 µm | <= 106 µm | 0.05% retained; ISO 1624 |
SABIC PVC 673E Emulsion Polyvinyl Chloride Product Description: PVC 673E is a fine particle, medium-molecular weight PVC homopolymer, made by emulsion polymerization. It is designed for the manufacture of plastisols exhibiting high viscosi.. |
|||
Particle Size | <= 106 µm | <= 106 µm | 0.005% retained; ISO 1624 |
SABIC PVC 701E Emulsion Polyvinyl Chloride for Paste Preparation Product Description: PVC 701E is a fine particle, medium-molecular weight PVC homopolymer, made by emulsion polymerization. It is designed for the manufacture of plastisols exhibiting high viscosi.. |
|||
Particle Size | <= 106 µm | <= 106 µm | 0.001% retained; ISO 1624 |
SABIC PVC 703E Emulsion Polyvinyl Chloride for Paste Preparation Product Description: PVC 703E is a fine particle, medium-molecular weight PVC homopolymer, made by emulsion polymerization. It is designed for the manufacture of plastisols exhibiting high viscosi.. |
|||
Particle Size | <= 106 µm | <= 106 µm | 0.01% retained; ISO 1624 |
SABIC PVC 741E Emulsion Polyvinyl Chloride for Paste Preparation Product Description: PVC 741E is a fine particle, high molecular weight PVC homopolymer, made by emulsion polymerization. It is designed for the manufacture of plastisols exhibiting low viscositie.. |
|||
Particle Size | 106 µm | 106 µm | Maximum of 1% greater than |
H.C. Starck Amperit® 518.002 Agglomerated, Sintered Tungsten Carbide-Cobalt 88-12 (WC-CO) |
|||
Particle Size | 106 µm | 106 µm | Maximum of 1% greater than, WSC-Ni 92/8 |
H.C. Starck Amperit® 568.005 Tungsten Carbide-Nickel 92-8 - Nickel SF RC 60 65-35 Composition is of NiSF RC 60 only |
|||
Particle Size | 106 µm | 106 µm | Maximum of 10% greater than |
H.C. Starck Amperit® 847.6 Agglomerated Yttria (Y2O3) |
|||
Particle Size | 106 µm | 106 µm | Maximum of 10% greater than |
H.C. Starck Amperit® 821.6 Zirconia-Yttria 80-20 (ZrO2-Y2O3) |
|||
Particle Size | 106 µm | 106 µm | Maximum of 1% greater than |
H.C. Starck Amperit® 547.002 Tungsten Carbide-Nickel 88-12 (WC-Ni) |