SABIC PVC 703E Emulsion Polyvinyl Chloride for Paste Preparation

Category Polymer , Thermoplastic , Vinyl (PVC)
Manufacturer SABIC
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC PVC 703E Emulsion Polyvinyl Chloride for Paste Preparation.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: PVC 703E is a fine particle, medium-molecular weight PVC homopolymer, made by emulsion polymerization. It is designed for the manufacture of plastisols exhibiting high viscosity and high yield value at low shear rates with pseudoplastic flow characteristics at high shear rates with plasticizer concentrations of >70 Phr. Because of the high viscosity of PVC 703E pastes, this resin is recommended primarily for highly plasticized applications. Plastisols made from this resin exhibit the following main properties:Low gelation temperatureLong shelf life, low viscosity agingLittle tendency to sedimentGood thermal stability with a range of standard stabilizersTypical Applications: PVC 703E has been developed for making plastisols of high yield points and high viscosity, without adding thickening agents. PVC 703E plastisols are ideal for chemical foams of very good quality with very regular closed cell structure, over a large range of oven temperatures.Information provided by SABIC.
Physical Properties Metric English Comments
Bulk Density 0.320 g/cc
0.0116 lb/in³
ISO 60
Volatiles <= 0.30 %
<= 0.30 %
ISO 1269
Particle Size <= 63 µm
<= 63 µm
1% retained; ISO 1624
<= 106 µm
<= 106 µm
0.001% retained; ISO 1624
Viscosity 5000 cP

@Pressure 0.621 MPa
5000 cP

@Pressure 90.0 psi
Servers; ASTM D-1823
Brookfield Viscosity 70000 cP
70000 cP
20 rpm; ISO 2555/4575
Descriptive Properties Value Comments
K-Value 70
ISO 1628-2