Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 8.94 g/cc | 0.323 lb/in³ | |
Materion ToughMet® T3 AT110 (OD≥4") ToughMet® is Brush Wellman's solution for severe service material problems. By applying their EquaCast® process, tailored alloying additions and spinodal hardening technology, they have e.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | |
Materion ToughMet® T3 AT90 (OD≥4") ToughMet® is Brush Wellman's solution for severe service material problems. By applying their EquaCast® process, tailored alloying additions and spinodal hardening technology, they have e.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | |
Materion ToughMet® T3 CX105 (OD≥4") ToughMet® is Brush Wellman's solution for severe service material problems. By applying their EquaCast® process, tailored alloying additions and spinodal hardening technology, they have e.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | |
Materion Alloy M65 (C17465) Beryllium Copper Rod Alloy M65 (C17465) is a machinable, high-performance, copper beryllium rod alloy from Brush Wellman. M65 has excellent strength, conductivity, and resistance to elevated temperature stress relaxatio.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | |
Lucas-Milhaupt Silvaloy® 25 Brazing Alloy Silvaloy 25 is historically a modification of Silvaloy 30 with a further reduction in silver content resulting in a higher melting point and a longer melting range. Silvaloy 25 is used for brazing s.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 151 ZHC® COPPER, 1/2 Hard Alloy C151 has excellent solderability, high conductivity, and good strength. C151 has superior high temperature softening resistance compared to pure copper C110.Applications can be found in high c.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 151 ZHC® COPPER, Extra Hard Alloy C151 has excellent solderability, high conductivity, and good strength. C151 has superior high temperature softening resistance compared to pure copper C110.Applications can be found in high c.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 151 ZHC® COPPER, Hard Alloy C151 has excellent solderability, high conductivity, and good strength. C151 has superior high temperature softening resistance compared to pure copper C110.Applications can be found in high c.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 18665 MSP1, 1/4 Hard MSP-1 high performance copper alloy with magnesium has high conductivity (63% IACS), high strength and excellent thermal creep properties. Typical uses include terminals, connectors, relays, springs.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 18665 MSP1, Annealed MSP-1 high performance copper alloy with magnesium has high conductivity (63% IACS), high strength and excellent thermal creep properties. Typical uses include terminals, connectors, relays, springs.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 18665 MSP1, Hard MSP-1 high performance copper alloy with magnesium has high conductivity (63% IACS), high strength and excellent thermal creep properties. Typical uses include terminals, connectors, relays, springs.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 19210 XP-10 Copper Iron, 1/2 Hard 19210 has higher strengths than most copper alloys but thanks to its composition and processing it retains formability and conductivity that other copper alloys lose. Typical uses include cooling f.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 19210 XP-10 Copper Iron, Extra Hard 19210 has higher strengths than most copper alloys but thanks to its composition and processing it retains formability and conductivity that other copper alloys lose. Typical uses include cooling f.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 706 Copper Nickel 10%, 1/4 Hard 706 exhibits excellent corrosion resistance, especially in marine applications. It has a relatively high strength and has resistance at elevated temperatures. The cost is relatively high compared to.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 706 Copper Nickel 10%, Annealed 706 exhibits excellent corrosion resistance, especially in marine applications. It has a relatively high strength and has resistance at elevated temperatures. The cost is relatively high compared to.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 706 Copper Nickel 10%, Hard 706 exhibits excellent corrosion resistance, especially in marine applications. It has a relatively high strength and has resistance at elevated temperatures. The cost is relatively high compared to.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 706 Copper Nickel 10%, Spring 706 exhibits excellent corrosion resistance, especially in marine applications. It has a relatively high strength and has resistance at elevated temperatures. The cost is relatively high compared to.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 715 Copper Nickel 30%, 1/2 Hard 715 exhibits excellent corrosion resistance, especially in marine applications. It has moderately high strength and has good creep resistance at elevated temperatures. The cost is relatively high co.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 715 Copper Nickel 30%, Extra Hard 715 exhibits excellent corrosion resistance, especially in marine applications. It has moderately high strength and has good creep resistance at elevated temperatures. The cost is relatively high co.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 101 OFE COPPER (Certified), 3/4 Hard Alloy 101 is known as Oxygen-Free Electronic (OFE). It reaches a minimum of 101% IACS conductivity rating. It is the most expensive out of the 101- 110 group because of its higher purity.Information.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 101 OFE COPPER (Certified), Annealed Alloy 101 is known as Oxygen-Free Electronic (OFE). It reaches a minimum of 101% IACS conductivity rating. It is the most expensive out of the 101- 110 group because of its higher purity.Information.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 102 OF COPPER (Non-Certified), 1/2 Hard Alloy 102 is an oxygen-free copper which has better forming, resistance to hydrogen embrittlement, and brazing characteristics than C110 ETP. C102 has good solder-ability and corrosion resistance an.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 102 OF COPPER (Non-Certified), 3/4 Hard Alloy 102 is an oxygen-free copper which has better forming, resistance to hydrogen embrittlement, and brazing characteristics than C110 ETP. C102 has good solder-ability and corrosion resistance an.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 102 OF COPPER (Non-Certified), Annealed Alloy 102 is an oxygen-free copper which has better forming, resistance to hydrogen embrittlement, and brazing characteristics than C110 ETP. C102 has good solder-ability and corrosion resistance an.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 102 OF COPPER (Non-Certified), Extra Spring Alloy 102 is an oxygen-free copper which has better forming, resistance to hydrogen embrittlement, and brazing characteristics than C110 ETP. C102 has good solder-ability and corrosion resistance an.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | |
Cadi C10100 Oxygen Free Copper Oxygen Free Copper is specified when resistance to hydrogen embrittlement is required due to application in a high temperature, hydrogen environment.Forms: RodBarPlateInformation provided by Cadi Co.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | |
Carlson 70 30 Cu Ni Copper-Nickel Alloy General DescriptionCarlson alloy 70 30 Cu Ni is a copper nickel alloy with excellent resistance to corrosion and erosion. It is strong and ductile. 70 30 Cu Ni is utilized in areas where high temp.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | |
ATI Allvac® Nickelvac® C-276 UNS N10276 Nickel Superalloy Uses: Pressure vessels, pumps, valves, HX tubing and piping for the CPI and HPI. Trays, flanges, fasteners, wire, screens.Property values are for samples in the metallurgical condition: 2050°F anne.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | |
ATI Allvac® Nickelvac® HC-276 Nickel Superalloy, Heat Treatment: 1121°C (2050°F) Anneal Data provided by Allvac.Applications: High temperature applications also requiring good resistance to corrosive fluids, such as liquids and combustion products. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | |
Materion ToughMet® T3 AT110 (OD ToughMet® is Brush Wellman's solution for severe service material problems. By applying their EquaCast® process, tailored alloying additions and spinodal hardening technology, they have engin.. |