Zell-Metall Engineering Plastics Zellamid 1400 (PET) at 50% RH

Category	Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Unreinforced
Manufacturer	Zell-Metall Engineering Plastics
Trade Name	Zellamid
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Zell-Metall Engineering Plastics Zellamid 1400 (PET) at 50% RH.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Zellamid® 1400 is the registered trademark of Zell-Metall’s partly crystalline thermoplastic Polyester based on Polyethylene Terephthalate.This PETP features outstanding dimensional stability, as it is virtually unaffected by ambient moisture. A low coefficient of friction and excellent wear resistance combined with low creep and high modulus make this the choice material for moving parts. Hot water resistance is low.Zellamid® 1400 is produced without centerline porosity. This material exhibits properties which make it suited to particular applications, especially high precision components.Typical applications are components for foodprocessing machines, mandrels, liquid and gas proof parts, electrical engineering and all parts where Acetal’s microporosity in the centerline is not desirable.For friction applications we offer Zellamid® 1400T (PETP with a solid lubricant) which shows a significantly reduced friction coefficient and increased resistance to wear.

Physical Properties	Metric	English	Comments
Density	1.36 g/cc	0.0491 lb/in³	Dry Density
Moisture Absorption at Equilibrium	0.23 %	0.23 %	Saturation at 50% RH; ISO 1110; DIN 53714
Water Absorption at Saturation	0.50 %	0.50 %	23°C; ISO 62; DIN 53495

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	80.0 MPa	11600 psi	ISO 527; DIN 53455
Elongation at Break	20 %	20 %	ISO 527; DIN 53455
Tensile Modulus	3.20 GPa	464 ksi	ISO 527; DIN 53452
Charpy Impact Unnotched	8.20 J/cm² @Temperature 23.0 °C	39.0 ft-lb/in² @Temperature 73.4 °F	ISO 179; DIN 53453
Charpy Impact, Notched	1.40 J/cm²	6.66 ft-lb/in²	double V-notch, rk=1.5 mm; DIN 53753
Dart Drop, Total Energy	80.0 J	59.0 ft-lb	DIN 53443

Thermal Properties	Metric	English	Comments
Melting Point	255 °C	491 °F	ISO 1218 Method A; DIN 53736
Maximum Service Temperature, Air	100 °C	212 °F	20,000 hours; 50% Tensile Strength; IEC 216; DIN 53446
	115 °C	239 °F	5000 hours; 50% Tensile Strength; IEC 216; DIN 53446
	160 °C	320 °F	a few hours operation
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
Flame Spread	<= 100 mm/min	<= 3.94 in/min	FMVSS - 302 flame propagation rate; DIN 75200

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	>= 450 V	>= 450 V	KA Method; IEC 112; DIN 53480
	>= 600 V	>= 600 V	KC Method; IEC 112; VDE 0303T1

Descriptive Properties	Value	Comments
Time yield limit	12 MPa	23°C, s1/1000; ISO.899 DIN.53444