Wolf Kunststoff ZEDEX® ZX-530EL3 066 Polymer Alloy, Carbon Fiber Reinforced

Category	Polymer , Thermoplastic
Manufacturer	Wolf Kunststoff
Trade Name	ZEDEX®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Wolf Kunststoff ZEDEX® ZX-530EL3 066 Polymer Alloy, Carbon Fiber Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Main Characteristics: Low thermal expansion; High rigidity; High yield stress; High wear resistance; Low friction; Stress ResistantApplications: Chemical Engineering; Laboratory Technology; Automitve Technology; Machine ToolsInformation provided by Zedex

Physical Properties	Metric	English	Comments
Density	1.47 g/cc	0.0531 lb/in³	ISO 1183
Water Absorption	0.010 % @Temperature 23.0 °C	0.010 % @Temperature 73.4 °F	RMC 93%; DIN EN ISO 62
Moisture Absorption at Equilibrium	0.050 %	0.050 %	DIN EN ISO 62

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	>= 100	>= 100	DIN 53505
Hardness, Shore D	86	86	DIN 53505
Ball Indentation Hardness	157 MPa	22800 psi	DIN 2039
Tensile Strength at Break	79.0 MPa	11500 psi	DIN EN ISO 527
Tensile Strength	79.0 MPa	11500 psi	DIN EN ISO 527
Tensile Stress	22.0 MPa @Strain 1.00 %, Time 3.60e+6 sec	3190 psi @Strain 1.00 %, Time 1000 hour	DIN 53444
Tensile Strength, Yield	50.6 MPa	7340 psi	Elastic Limit
Elongation at Break	5.0 %	5.0 %	Flexural; DIN EN ISO 178
	5.0 %	5.0 %	DIN EN ISO 527
Elongation at Yield	2.1 %	2.1 %	Elastic Yield Point
	3.7 %	3.7 %	Flexural; DIN EN ISO 178
	5.0 %	5.0 %	Elongation at Maximum Force; DIN EN ISO 527
Tensile Modulus	3.94 GPa	571 ksi	DIN EN ISO 527
Flexural Strength	114 MPa	16500 psi	Outer Fiber Stress at 3.5% Outer Fiber Strain; DIN EN ISO 178
	116 MPa	16800 psi	DIN EN ISO 178
	116 MPa	16800 psi	DIN EN ISO 178
Flexural Modulus	4.356 GPa	631.8 ksi	DIN EN ISO 178
Compressive Strength	70.0 MPa	10200 psi	Elastic Limit
	150 MPa	21800 psi	break; DIN EN ISO 604
	150 MPa	21800 psi	DIN EN ISO 604
	30.0 MPa @Time 3.60e+7 sec	4350 psi @Time 10000 hour
	60.0 MPa @Time 360000 sec	8700 psi @Time 100 hour
	75.0 MPa @Time 36.0 sec	10900 psi @Time 0.0100 hour
	46.0 MPa @Strain 3.50 %	6670 psi @Strain 3.50 %	DIN EN ISO 604
Compressive Modulus	3.50 GPa	508 ksi	DIN EN ISO 604
Fatigue Strength	41.0 MPa @# of Cycles 1.00e+6	5950 psi @# of Cycles 1.00e+6	1 Hz
K Factor (ISO)	0.50 µm/km @Temperature 100 °C	0.50 µm/km @Temperature 212 °F
	1.0 µm/km @Temperature 20.0 °C	1.0 µm/km @Temperature 68.0 °F
	4.3 µm/km @Temperature 200 °C	4.3 µm/km @Temperature 392 °F
	7.7 µm/km @Temperature 240 °C	7.7 µm/km @Temperature 464 °F
Charpy Impact Unnotched	1.30 J/cm²	6.19 ft-lb/in²	EN ISO 179/1eU
Charpy Impact, Notched	0.550 J/cm²	2.62 ft-lb/in²	EN ISO 179/1eA
Coefficient of Friction, Dynamic	0.15 @Temperature 100 °C	0.15 @Temperature 212 °F	Dry Operation
	0.16 @Temperature 20.0 °C	0.16 @Temperature 68.0 °F	Dry Operation
Coefficient of Friction, Static	0.18 @Temperature 20.0 °C	0.18 @Temperature 68.0 °F	Dry Operation
Tensile Creep Modulus, 1000 hours	2180 MPa	316000 psi	At 1% Deformation; DIN 53444
Limiting Pressure Velocity	0.06667 MPa-m/sec	1903 psi-ft/min	v = 200m/min
	0.200 MPa-m/sec	5710 psi-ft/min	v = 100m/min
	0.430 MPa-m/sec	12300 psi-ft/min	v = 1m/min
	0.915 MPa-m/sec	26100 psi-ft/min	v = 10m/min
Compression Set	5.0 %	5.0 %	Elastic Compression Limit
	7.2 %	7.2 %	Nominal Compressive Yield Strain; DIN EN ISO 604
	30 %	30 %	Nominal Compressive Strain at Compressive Strength; DIN EN ISO 604

Thermal Properties	Metric	English	Comments
CTE, linear	38.0 µm/m-°C @Temperature <=100 °C	21.1 µin/in-°F @Temperature <=212 °F	ISO E 830
	50.0 µm/m-°C @Temperature <=150 °C	27.8 µin/in-°F @Temperature <=302 °F	ISO E 831
Specific Heat Capacity	0.840 J/g-°C	0.201 BTU/lb-°F	DSC
Melting Point	320 °C	608 °F	DSC
Maximum Service Temperature, Air	90.0 °C	194 °F	Pressed Bushings
	240 °C	464 °F	Continuous
	260 °C	500 °F	Short Term (3h)
Deflection Temperature at 1.8 MPa (264 psi)	260 °C	500 °F	DIN EN ISO 75
Glass Transition Temp, Tg	90.0 °C	194 °F	DSC
Flammability, UL94	V-0	V-0

Electrical Properties	Metric	English	Comments
Volume Resistivity	71000 ohm-cm	71000 ohm-cm	IEC 93
Surface Resistance	69000 ohm	69000 ohm	IEC 93
Dielectric Constant	4.3 @Frequency 110 Hz	4.3 @Frequency 110 Hz	IEC 250
Dielectric Strength	0.100 kV/mm	2.54 kV/in	IEC 243
Dissipation Factor	0.025	0.025	IEC 112
	0.064 @Frequency 1.00 Hz	0.064 @Frequency 1.00 Hz

Descriptive Properties	Value	Comments
Alignment Adjustment	2	Nominal Scale: 1, low; 10, high
Chemical Sterilization	10	Nominal Scale: 1, low; 10, high
Color	Grey
Creep Resistance	7	Nominal Scale: 1, low; 10, high
Dimensional Stability with Thermal Expansion	7	Nominal Scale: 1, low; 10, high
Free from Silicon	Applicable
Gamma-rays Radiation Sterilization	4	Nominal Scale: 1, low; 10, high
Injection Molded Parts	Applicable
Machined Parts	Applicable
Moist Heat Sterilization	6	Nominal Scale: 1, low; 10, high
Plastic Granules	Applicable
Rate of Desorption	3.12E-07	a = .49
Resistance Against dust, Dirt, Abrasive Substances	6	Nominal Scale: 1, low; 10, high
Resistance Against Hot Water	140
Resistance to Chemicals	9	Nominal Scale: 1, low; 10, high
Resistant Against Disinfectant	Applicable
Rods up to Øe (de)	Applicable
Sheets up to Maximum Thickness	Applicable
Sliding Velocity	100
Suitable for Outdoor Use	7	Nominal Scale: 1, low; 10, high
Suitable for Use in Water	Applicable
Suitable for Vacuum	Applicable
Tubes (hollow rods) up to Øe (de)	Applicable
UV Rays Resistance	8	Nominal Scale: 1, low; 10, high
UV-Sterilization	7	Nominal Scale: 1, low; 10, high