Weartech International WT-1 Cobalt Hardfacing & Wear Resistant Alloy
| Category | Metal , Nonferrous Metal , Cobalt Alloy |
| Manufacturer | Weartech |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Weartech International WT-1 Cobalt Hardfacing & Wear Resistant Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: seaming rolls, valve seats, wear pads, pump sleeves, seals, bearings, bushings, saw blades, cuttersInformation provided by Weartech International
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.73 g/cc | 0.315 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell C | 48 - 59 | 48 - 59 | |
| Hardness, Vickers | 100 @Treatment Temp. 760 °C |
100 @Treatment Temp. 1400 °F |
|
| 250 @Treatment Temp. 649 °C |
250 @Treatment Temp. 1200 °F |
||
| 400 @Treatment Temp. 538 °C |
400 @Treatment Temp. 1000 °F |
||
| 475 @Treatment Temp. 427 °C |
475 @Treatment Temp. 800 °F |
||
| 545 @Treatment Temp. 25.0 °C |
545 @Treatment Temp. 77.0 °F |
||
| Tensile Strength | 483 MPa | 70000 psi | As Cast |
| Elongation at Yield | 0.00 - 1.0 % | 0.00 - 1.0 % | |
| Charpy Impact | 5.42 J | 4.00 ft-lb | As Cast |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.7 µm/m-°C | 7.60 µin/in-°F | |
| Specific Heat Capacity | 0.397 J/g-°C | 0.0950 BTU/lb-°F | |
| Melting Point | <= 1260 °C | <= 2300 °F | |
| Liquidus | 1260 °C | 2300 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 2.3 % | 2.3 % | |
| Chromium, Cr | 30 % | 30 % | |
| Cobalt, Co | 47.9 - 53.9 % | 47.9 - 53.9 % | |
| Iron, Fe | <= 3.0 % | <= 3.0 % | |
| Nickel, Ni | <= 3.0 % | <= 3.0 % | |
| Silicon, Si | 0.80 % | 0.80 % | |
| Tungsten, W | 13 % | 13 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Corrosion Resistance, Hydrochloric Acid Conc. 5.65% | >20 mils/year | RT |
| >400 mils/year | Boiling | |
| Corrosion Resistance, Nitric Acid Conc. 25-65% | >20 mils/year | RT |
| >400 mils/year | Boiling | |
| Corrosion Resistance, Sulfuric Acid Conc. 5-10% | >20 mils/year | RT |
| >400 mils/year | 150 °F | |
| Relative Wear Performance | Cold Abrasion | Excellent |
| Corrosion | Excellent | |
| Erosion | Excellent | |
| Hot Abrasion | Excellent | |
| Impact | Not Recommended | |
| Metal to Metal | Excellent |
Users viewing this material also viewed the following:
- Park Electrochemical Nelcote® P-600 Polyester Prepreg, 7781 E-Glass Reinforced
- Lucas-Milhaupt BRAZE 600 Silver Based Cadmium Free Filler Metal
- Latrobe Graph-Air® Cold Work Tool Steel (ASTM A10)
- Techmer ES HiFill® PA6/6 GF/M40 ML2 GY 40% Glass/Mineral Fiber Filled
- Solvay MACKAM® OAB Surfactant
- A. Schulman POLYPUR™ FPU 1377 Thermoplastic Polyurethane Compound
- Total PPH 9040 Polypropylene, Homopolymer
- Chosun Refractories AM10S Alumina Magnesia Carbon Bricks for Ladle Wall And Bottom
- Arlon 44576R009A 0.0058" (0.216 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Oxford Polymers PC 1518 Unfilled Polycarbonate for Injection Molding
Copyright © lookpolymers.com All Rights Reserved