Wanhua Chemical Wanthane® WHT-1290 Polyester Based TPU
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane TPE , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Polyester Grade |
| Manufacturer | Wanhua Chemical Group Co., Ltd. |
| Trade Name | Wanthane® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Wanhua Chemical Wanthane® WHT-1290 Polyester Based TPU.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Good mechanical properties, good extrusion stability, low costInformation provided by Wanhua Chemical Group Co., Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 91 | 91 | ASTM D2240 |
| Tensile Strength | 28.0 MPa | 4060 psi | ASTM D412 |
| Elongation at Break | 500 % | 500 % | ASTM D412 |
| 100% Modulus | 0.00800 GPa | 1.16 ksi | ASTM D412 |
| 300% Modulus | 0.0150 GPa | 2.18 ksi | ASTM D412 |
| Tear Strength | 110 kN/m | 628 pli | ASTM D624 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 185 - 205 °C | 365 - 401 °F |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PP HIP15025 HC Polypropylene
- Eastman 5282 LDPE 8% EVA Copolymer, High Clarity, High Impact Film Resin (discontinued **)
- Lehmann & Voss LUVOCOM® 19-8373 Polyamide 46, with carbon fiber, lubricant modified
- Solvay Specialty Polymers solvene® T 2808 Electroactive Polymer (EAP)
- American Elements Tantalum Nanoparticles
- ExxonMobil Pax-Plus™ 3201 Blown Film Resin
- Cadi 150 Copper Alloy
- 3D Systems Accura® Amethyst™ Plastic for Viper™ SLA® Systems
- ATI Allegheny Ludlum Stainless Steel Type 301, annealed (UNS S30100)
Copyright © lookpolymers.com All Rights Reserved