Vyncolit W5000 Glass Fiber and Mineral Filled Novolac Phenolic

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Mineral/Glass Filled
Manufacturer Vyncolit N.V., Sumitomo Bakelite
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Vyncolit W5000 Glass Fiber and Mineral Filled Novolac Phenolic.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Novolac resin based, glass fiber and mineral filled. Excellent dimensional stability and very low coefficient of linear expansion and excellent chemical resistance at elevated temperatures in several hydraulic brake fluids. Specially used for Brake systems.Information provided by Sumitomo Bak North America, Inc.
Physical Properties Metric English Comments
Bulk Density 1.03 g/cc
0.0372 lb/in³
ISO 60
Density 2.08 g/cc
0.0751 lb/in³
ISO 1183
Water Absorption 0.060 %
0.060 %
ISO 62
Linear Mold Shrinkage 0.0015 cm/cm
0.0015 in/in
ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 90.0 MPa
13100 psi
ISO 527-1
Elongation at Break 0.40 %
0.40 %
ISO 527-1
Tensile Modulus 29.0 GPa
4210 ksi
ISO 527-1
Flexural Strength 180 MPa
26100 psi
ISO 178
Flexural Modulus 24.0 GPa
3480 ksi
ISO 178
Compressive Strength 360 MPa
52200 psi
ISO 604
Charpy Impact Unnotched 0.850 J/cm²
4.04 ft-lb/in²
ISO 179-1
Charpy Impact, Notched 0.280 J/cm²
1.33 ft-lb/in²
ISO 179-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 14.0 µm/m-°C
7.78 µin/in-°F
TMA
CTE, linear, Transverse to Flow 25.0 µm/m-°C
13.9 µin/in-°F
TMA
Deflection Temperature at 1.8 MPa (264 psi) >= 211 °C
>= 412 °F
ISO 75 Af
Flammability, UL94 V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
Shrinkage 0.020 %
0.020 %
Post Shrinkage; ISO 2577
Descriptive Properties Value Comments
Color Dark Green
Molding Method Compression
Injection
Transfer