Vyncolit TX10916/15 Graphite Filled Novolac Phenolic
| Category | Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic |
| Manufacturer | Vyncolit N.V., Sumitomo Bakelite |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Vyncolit TX10916/15 Graphite Filled Novolac Phenolic.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Novolac resin based, graphite filled compound used for low friction applications where dimensional stability is requiredInformation provided by Sumitomo Bak North America, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.860 g/cc | 0.0311 lb/in³ | ISO 60 |
| Density | 1.69 g/cc | 0.0611 lb/in³ | ISO 1183 |
| Water Absorption | 0.050 % | 0.050 % | ISO 62 |
| Linear Mold Shrinkage | 0.0043 cm/cm | 0.0043 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 56.0 MPa | 8120 psi | ISO 527-1 |
| Elongation at Break | 0.38 % | 0.38 % | ISO 527-1 |
| Tensile Modulus | 18.0 GPa | 2610 ksi | ISO 527-1 |
| Flexural Strength | 93.0 MPa | 13500 psi | ISO 178 |
| Flexural Modulus | 16.0 GPa | 2320 ksi | ISO 178 |
| Compressive Strength | 166 MPa | 24100 psi | ISO 604 |
| Charpy Impact Unnotched | 0.360 J/cm² | 1.71 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 0.140 J/cm² | 0.666 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 14.0 µm/m-°C | 7.78 µin/in-°F | TMA |
| CTE, linear, Transverse to Flow | 32.0 µm/m-°C | 17.8 µin/in-°F | TMA |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 175 °C | >= 347 °F | ISO 75 Af |
| Shrinkage | 0.090 % | 0.090 % | Post Shrinkage; ISO 2577 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black | |
| Molding Method | Compression | |
| Injection | ||
| Transfer |
Users viewing this material also viewed the following:
- RheTech Products T10P102-00EG 10% Talc Reinforced Polypropylene, Extrusion Grade, Natural
- Hong Kun Group 3-(Trifluoromethyl)cinnamic Acid Pharmaceutical Intermediate
- Karina E 39/81-IE MBU Pink Color Concentrate
- Tra-Con Tra-Bond 575T01 Anaerobic Adhesive
- Loctite® 3201 Light Cure Acrylic Adhesive
- A. Schulman LP477-01 High-Density Polyethylene
- Arkema Group EVATANE® 28-800 Copolymer Ethylene - Vinyl Acetate
- Tipco Tipcofil® AGM 802 - 25% Mineral & 15% Glass Fiber Reinforced Nylon-6 Compound, with High Heat Stability
- CeramTec Rubalit® A 1898 Alumina, 98%
Copyright © lookpolymers.com All Rights Reserved