UBE UBEPOL BR360L Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C)
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | UBE |
| Trade Name | UBEPOL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | UBE UBEPOL BR360L Non-Oil Extended Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: UBEPOL BR is UBE's line of polybutadiene rubber products.Information provided by UBE.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 64 | 64 | ASTM D412 |
| Tensile Strength at Break | 19.1 MPa | 2770 psi | ASTM D412 |
| Elongation at Break | 500 % | 500 % | ASTM D412 |
| 100% Modulus | 0.00230 GPa | 0.334 ksi | ASTM D412 |
| 200% Modulus | 0.00560 GPa | 0.812 ksi | ASTM D412 |
| 300% Modulus | 0.0106 GPa | 1.54 ksi | ASTM D412 |
| Rebound | 61 % | 61 % | BS.903,PART22 |
| Tear Strength | 53.0 kN/m | 302 pli | ASTM D624 |
| Abrasion | 111 | 111 | Lombourn Abrasion Index (Iwamoto Seisakusyo, Japan); UBE Method |
| 241 | 241 | Pico Abrasion Index; ASTM D2228 | |
| Compression Set | 13 % | 13 % | Method B, 70°C, 72hrs; ASTM D395 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Cut Generation De Mattia Flexing Machine | Min 300,000 times | ASTM D430 |
| Cut Growth (2mm-->15mm) De Mattia Flexing Machine | 1900 times | ASTM D313 |
| Goodrich Flex, 0.175" Stroke, 55lb, 100°C, P.S. | 5% | ASTM D623 (24°C change in temperature) |
| Wet Skid Resistance on Safety-Walk | 17 | UBE Method (British Portable Skid Resistance Tester) |
Users viewing this material also viewed the following:
- Outokumpu 4438 High Performance Austenitic Stainless Steel
- Radici Radilon® A HSX88 (cond.) Nylon 66
- Solvay Specialty Polymers Ryton® R-4-220BL Polyphenylene Sulfide Compound (Unverified Data**)
- Garlock 19 SBR Rubber Gasketing, Cotton Reinforced
- Jackon JACKOCELL® R311 Expanded Polystyrene Packaging and Shape Molding
- A. Schulman POLYFLAM™ RPP 1174 Talc Filled, Homopolymer Polypropylene
- Cossa Polimeri ESTABLEND 4501 V0/D Flame Retardant PC - ABS
- ChevronTexaco Mechanism LPS® ISO 15 Hydraulic Oil
- Dow LIGHTER™ C93 Polyethylene Terephthalate (PET) Resin
- ATI Allegheny Ludlum Stainless Steel Type 201, 10% Cold Work (UNS S20100)
Copyright © lookpolymers.com All Rights Reserved