Toyobo Vylopet® EMC405A PET/PBT Blend

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PET + PBT Unreinforced , Polyethylene Terephthalate (PET)
Manufacturer Toyobo
Trade Name VYLOPET®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Toyobo Vylopet® EMC405A PET/PBT Blend.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Key Feature: HB UL-94 ClassApplications: glossy surface componentsPET/PBT blends suggested for glossy surfaces. General features of Vylopet® include heat resistance, good mechanical properties, high dielectric strength and tracking resistance, chemical & weather resistance, and processability.Information provided by Toyobo Co., Ltd
Physical Properties Metric English Comments
Density 1.45 g/cc
0.0524 lb/in³
ASTM D792
Water Absorption 0.050 %
0.050 %
ASTM D570
Linear Mold Shrinkage 0.012 cm/cm
0.012 in/in
Linear Mold Shrinkage, Transverse 0.013 cm/cm
0.013 in/in
Mechanical Properties Metric English Comments
Hardness, Rockwell M 90
90
ASTM D785
Tensile Strength, Ultimate 53.0 MPa
7690 psi
ASTM D638
Elongation at Break 3.7 %
3.7 %
ASTM D638
Flexural Yield Strength 88.0 MPa
12800 psi
ASTM D790
Flexural Modulus 4.70 GPa
682 ksi
ASTM D790
Compressive Yield Strength 59.0 MPa
8560 psi
ASTM D695
Izod Impact, Notched 0.700 J/cm
1.31 ft-lb/in
ASTM D256
Taber Abrasion, mg/1000 Cycles 15
15
ASTM D1044
Thermal Properties Metric English Comments
Melting Point 255 °C
491 °F
DSC
Deflection Temperature at 0.46 MPa (66 psi) 200 °C
392 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 120 °C
248 °F
ASTM D648
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Dielectric Strength 24.0 kV/mm

@Thickness 2.00 mm
610 kV/in

@Thickness 0.0787 in
ASTM D149
Arc Resistance 130 sec
130 sec
ASTM D495
Comparative Tracking Index 255 V
255 V
IEC test