Toyobo VYLOPET® EMC132-01 Injection Molding Polyester Resin, Flame Resistant
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | Toyobo |
| Trade Name | VYLOPET® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo VYLOPET® EMC132-01 Injection Molding Polyester Resin, Flame Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Relay partsFeatures: Excellent arc resistanceFlame resistanceInformation provided by Toyobo.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in³ | ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | MD |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 95 | 95 | ASTM D785 |
| Tensile Strength at Break | 145 MPa | 21000 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 220 MPa | 31900 psi | ASTM D790 |
| Flexural Modulus | 12.0 GPa | 1740 ksi | ASTM D790 |
| Izod Impact, Notched | 0.770 J/cm | 1.44 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C @Temperature 20.0 °C |
16.7 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Melting Point | 255 °C | 491 °F | By DSC |
| Maximum Service Temperature, Air | 130 °C | 266 °F | Thermal index; ASTM UL746B |
| 225 °C | 437 °F | Ball pressure temperature; IEC Method | |
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.7937 mm |
V-0 @Thickness 0.03125 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 25.0 kV/mm @Thickness 2.00 mm |
635 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Arc Resistance | 83 sec | 83 sec | Tungsten electrode; ASTM D495 |
| Comparative Tracking Index | 175 - 249 V | 175 - 249 V | IEC Pub1.112, class 3; IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 260 °C | 482 - 500 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F |
Users viewing this material also viewed the following:
- MV Labs LI410 LiCl·H2O Lithium chloride hydrate
- MarkeTech Aluminum Oxide Ceramic - Alumina 97.5%
- MarkeTech Repton 201 Aluminum Oxide
- KKPC Kuhmo HI 425TVL High Flow/High Heat Resistant HIPS
- Solvay Specialty Polymers Solef® 20808 Polyvinylidene Fluoride (PVDF)
- Sibur 21030-PM1 Polypropylene with Low Haze
- Solvay ALKAMULS® RC Surfactant
- Chosun Refractories A-4 Insulating Firebrick
- BASF Diisopropanolamine 90% Solution
Copyright © lookpolymers.com All Rights Reserved