- Total LDPE 1022 FN 24 Low Density Polyethylene - Blown Film
Total LDPE 1022 FN 24 Low Density Polyethylene - Blown Film
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | Total Atofina |
| Trade Name | LDPE |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Total LDPE 1022 FN 24 Low Density Polyethylene - Blown Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LDPE 1022 FN 24 is a low density polyethylene made by a high pressure process without antioxidant.LDPE 1022 FN 24 is suited to many applications in the field of consumer, industrial, food or hygiene packaging such as bags, lamination and coextrusion film.Information provided by Total Petrochemicals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.923 g/cc | 0.923 g/cc | ISO 1183 |
| Thickness | 40.0 microns | 1.57 mil | for samples tested on this data sheet |
| 25.0 - 150 microns | 0.984 - 5.91 mil | possible range, depending on extrusion conditions | |
| Melt Flow | 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.3 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 12.0 MPa | 1740 psi | ISO 527-3 |
| Film Tensile Strength at Yield, TD | 11.5 MPa | 1670 psi | ISO 527-3 |
| Film Elongation at Break, MD | 360 % | 360 % | ISO 527-3 |
| Film Elongation at Break, TD | 630 % | 630 % | ISO 527-3 |
| Elmendorf Tear Strength, MD | 7.60 g/micron | 193 g/mil | ISO 6383-2 |
| Elmendorf Tear Strength, TD | 6.30 g/micron | 160 g/mil | ISO 6383-2 |
| Dart Drop Test | 95.0 g | 0.209 lb | ISO 7765-1 |
| Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 109 °C | 228 °F | ISO 11357 |
| Vicat Softening Point | 94.0 °C | 201 °F | ISO 306 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 7.0 % | 7.0 % | ISO 14782 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 150 - 190 °C | 302 - 374 °F |
Users viewing this material also viewed the following:
- Palm Labs Adhesives TURBO-LOCK SERIES 11-OR Anaerobic Thread Locking Compound
- Lehmann & Voss LUVOCOM® GS-H/2 Polyamide 66, lubricant modified
- SABIC Innovative Plastics NORYL GFN1740V PPE+PS (Europe-Africa-Middle East)
- Teknor Apex Sinvicomp SMG 10500 Polyvinyl Chloride, Flexible
- Formosa Plastics Formolene® 5143S Homopolymer Polypropylene
- A. Schulman POLYBATCH™ Redwood 10416U Concentrate Based In LLDPE
- Cheng Yu Plastic T890G3 PBT, 30% Glass Fiber
- Dow Corning C6-540 LIQUID SILICONE RUBBER KIT
- Arkema Group Rilsan® BZM 8 NOIR TL Nylon 11, 8% Glass Fiber Filled (Conditioned)
- Beijing Chemical Industry KAIFA® MN301-G35 Nylon 66 Resin
Copyright © lookpolymers.com All Rights Reserved