Total LDPE 1022 FH 24 Low Density Polyethylene - Blown Film

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer	Total Atofina
Trade Name	LDPE
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Total LDPE 1022 FH 24 Low Density Polyethylene - Blown Film.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LDPE 1022 FH 24 is a low density polyethylene made by a high pressure process.LDPE 1022 FH 24 is a slip and anti-block formulated grade.LDPE 1022 FH 24 is suited to many applications in the field of consumer, industrial, food or hygiene packaging such as bags, lamination and coextrusion film.Information provided by Total Petrochemicals.

Physical Properties	Metric	English	Comments
Specific Gravity	0.923 g/cc	0.923 g/cc	ISO 1183
Thickness	40.0 microns	1.57 mil	for samples tested on this data sheet
	20.0 - 150 microns	0.787 - 5.91 mil	possible range, depending on extrusion conditions
Melt Flow	2.3 g/10 min @Load 2.16 kg, Temperature 190 °C	2.3 g/10 min @Load 4.76 lb, Temperature 374 °F	ISO 1133
Antiblock Level	750 ppm	750 ppm	Talc
Slip Level	750 ppm	750 ppm	Erucamide

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	12.0 MPa	1740 psi	ISO 527-3
Film Tensile Strength at Yield, TD	11.5 MPa	1670 psi	ISO 527-3
Film Elongation at Break, MD	350 %	350 %	ISO 527-3
Film Elongation at Break, TD	580 %	580 %	ISO 527-3
Elmendorf Tear Strength, MD	7.30 g/micron	185 g/mil	ISO 6383-2
Elmendorf Tear Strength, TD	6.10 g/micron	155 g/mil	ISO 6383-2
Dart Drop Test	95.0 g	0.209 lb	ISO 7765-1
Film Tensile Strength at Break, MD	22.0 MPa	3190 psi	ISO 527-3
Film Tensile Strength at Break, TD	20.0 MPa	2900 psi	ISO 527-3

Thermal Properties	Metric	English	Comments
Melting Point	109 °C	228 °F	ISO 11357
Vicat Softening Point	94.0 °C	201 °F	ISO 306

Optical Properties	Metric	English	Comments
Haze	8.0 %	8.0 %	ISO 14782

Processing Properties	Metric	English	Comments
Processing Temperature	150 - 190 °C	302 - 374 °F