Total Finaprene® 602 Styrene-Butadiene TPE Copolymer Compound, Formulated to 59 Shore A  (discontinued **)

Category Polymer , Thermoplastic , Elastomer, TPE , Styrenic TPE , Styrene-Butadiene
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Total Finaprene® 602 Styrene-Butadiene TPE Copolymer Compound, Formulated to 59 Shore A  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Styrene-Butadiene CopolymerDescription: Finaprene® 602 is a thermoplastic elastomer type radial styrene-butadiene block copolymer. Thanks to its broad molecular weight distribution, Finaprene® 602 provides good fluidity properties to the compound while keeping good mechanical properties.Applications: Thanks to it very high crumb porosity Finaprene® 602 is designed for the compounding industry. This crumb shape, along with the broad molecular weight distribution confer a quick oil absorption to the polymer and lead to the production of fluid compounds. This fluidity will enhance the surface aspect of the injected article. The structure of 602 is n = 2, 3, 4, 5.Content of the compound for which the listed properties apply: F484: 0F435: 83F411x: 17F602: 0F507: 12.5GPPS: 32HIPS: 0Oil: 56CaCO3: 10Additional Notes: DIN Abrasion: 155 mm³Data provided by Total Petrochemicals.Total Petrochemicals includes former Fina and Atofina plastics product lines.
Physical Properties Metric English Comments
Density 0.9681 g/cc
0.03497 lb/in³
Finaprene 2602 Test
Melt Flow 26 g/10 min

@Load 5.00 kg,
Temperature 190 °C
26 g/10 min

@Load 11.0 lb,
Temperature 374 °F
Mechanical Properties Metric English Comments
Hardness, Shore A 59
59
Finaprene 1505 Test
Tensile Strength, Ultimate 5.70 MPa
827 psi
ASTM D638
Elongation at Break 515 %
515 %
ASTM D638
300% Modulus 0.00430 GPa
0.624 ksi
Tear Strength 26.1 kN/m
149 pli
Abrasion 155
155
mm³; DIN Abrasion