- Tipco Tipcofil® AG 200 - 10% Glass Fiber Reinforced Nylon-6 Compound, with High Heat Stability
Tipco Tipcofil® AG 200 - 10% Glass Fiber Reinforced Nylon-6 Compound, with High Heat Stability
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Tipco Industries Ltd., India |
| Trade Name | Tipcofil® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Tipco Tipcofil® AG 200 - 10% Glass Fiber Reinforced Nylon-6 Compound, with High Heat Stability.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
10% Glass Reinforced Nylon-6 CompoundApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Water Absorption | 1.3 % | 1.3 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM D955 |
| Melt Flow | 20 g/10 min | 20 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 110 MPa | 16000 psi | ASTM D638 |
| Elongation at Break | >= 4.0 % | >= 4.0 % | ASTM D638 |
| Flexural Yield Strength | 145 MPa | 21000 psi | ASTM D790 |
| Flexural Modulus | 4.10 GPa | 595 ksi | ASTM D790 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | ASTM D256 |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 190 °C | 374 °F | ASTM D648 |
| Vicat Softening Point | 200 °C | 392 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 240 °C | 464 °F | |
| Rear Barrel Temperature | 240 °C | 464 °F | |
| Middle Barrel Temperature | 245 °C | 473 °F | |
| Front Barrel Temperature | 255 °C | 491 °F | |
| Nozzle Temperature | 245 °C | 473 °F | |
| Mold Temperature | 85.0 °C | 185 °F | |
| Drying Temperature | 80.0 °C | 176 °F |
Users viewing this material also viewed the following:
- Pyrotek TS-111 Thermoset Electrical Insulation Product (Nema Grade: G-11)
- Momentive Performance Materials AC6111 Boron Nitride (BN) Powder
- Sawbones Cellular Rigid Polyurethane Foam 7.5 pcf Density
- Borealis LE0315 Polyethylene Compound, Crosslinkable, Semiconductive
- Zhejiang Juner 201-G0 Flame Resistant Nonreinforced
- Dow SiLK™ D Semiconductor Dielectric Resin
- DSM Arnitel® XG5855 TPC-ET
- Asahi Kasei Thermylon® NSG-240A-C 50% Ceramic and Glass Fiber Reinforced
- 3M Scotchcal™ 8662 Graphic Film
- Amity Thermosets ATR 126 Phenolic Molding Organic Filler, Injection Molded
Copyright © lookpolymers.com All Rights Reserved