- Thermoseal KLINGERSIL® C-4201 General Application Gasketing
Thermoseal KLINGERSIL® C-4201 General Application Gasketing
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Thermoseal Inc. |
| Trade Name | KLINGERSIL® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Thermoseal KLINGERSIL® C-4201 General Application Gasketing.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Synthetic FiberNitrile BinderExcellent Resistance to Oil & SolventsGood Anti-Stick PropertiesExcellent OEM MaterialInformation provided by Thermoseal Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.90 g/cc | 0.0686 lb/in³ | ASTM F1315 |
| Thickness | 1588 microns | 62.52 mil | Thickness tested |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 14.0 kV/mm | 356 kV/in | ASTM D149-95a |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | White or Black | (Top/Bottom) |
| Compressibility | 7 percent | ASTM F36J |
| Creep Relaxation | 20 percent | 1/32", ASTM F38B |
| Gas Permeability | <0.5 ml/min | DIN 3535/6 |
| Klinger Hot Compression Test | 11 percent | Initial, Thickness Decrease 73°F (23°C) |
| 19.5 percent | Additional, Thickness Decrease 572°F (300°C) | |
| Leachable Chloride Content | 200 ppm | FSA Method (Typical) |
| Recovery | >50 percent | ASTM F36J |
| Sealability | <0.5 ml/hr | 1/32", ASTM F37A |
| Thickness Increase | 0-5% | ASTM F146 after immersion in ASTM Oil 1, 5h/300°F (149°C) |
| 0-5% | ASTM Oil IRM903, 5h/300°F (149°C) | |
| 0-5% | ASTM Fuel A, 5h/73°F (23°C) | |
| 0-5% | ASTM Fuel B, 5h/73°F (23°C) | |
| Weight Increase | <10% | ASTM F146 after immersion in Fuel B 5h/73°F (23°C) |
Users viewing this material also viewed the following:
- RheTech Products FT4702-698UV Thermoplastic Polyolefin, UV Stabilized, RXF Jet Black
- Nye Lubricants 774VLF-MS (NG) Synthetic Oil
- Polymax® Maxelast® F02-137B TPE, Halogen Free Extrusion Grade
- Ineos Styrenics 166H General Purpose Polystyrene (NAFTA)
- Karina 801-27/13-IS-RG Smoky Clear PVC Compound
- Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 4000 hours
- Indorama AlphaPet Preformance® 1708CC(A) PET Resin
- Dow UNIVAL™ DMDA-6230 NT 7 High Density Polyethylene Resin (HDPE)
- California Fine Wire Stablohm 675 Nickel, Chromium and Iron Resistance Wire
Copyright © lookpolymers.com All Rights Reserved