Teknor Apex Chemlon® 340G Nylon 610, Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 610 , Nylon 610, Glass Reinforced |
| Manufacturer | Teknor Apex Company |
| Trade Name | Chemlon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teknor Apex Chemlon® 340G Nylon 610, Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Processing Method: Injection Molding Forms: PelletsInformation Provided by Teknor Apex
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | 24 hr; ASTM D750 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | ASTM D955 |
| Melt Flow | 5.00 g/10 min @Load 1.00 kg, Temperature 235 °C |
5.00 g/10 min @Load 2.20 lb, Temperature 455 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 165 MPa | 24000 psi | ASTM D638 |
| Elongation at Break | 2.7 % | 2.7 % | ASTM D638 |
| Elongation at Yield | 2.5 % | 2.5 % | ASTM D638 |
| Flexural Strength | 241 MPa | 35000 psi | ASTM D790 |
| Flexural Modulus | 9.17 GPa | 1330 ksi | ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm @Temperature 22.8 °C |
3.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 211 °C | 412 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.810 mm |
HB @Thickness 0.0319 in |
|
| Oxygen Index | 25 % | 25 % | ASTM D2863 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 235 - 252 °C | 455 - 485 °F | |
| Middle Barrel Temperature | 246 - 268 °C | 475 - 515 °F | |
| Front Barrel Temperature | 257 - 274 °C | 495 - 525 °F | |
| Nozzle Temperature | 252 - 279 °C | 485 - 535 °F | |
| Melt Temperature | 223 °C | 433 °F | |
| 252 - 277 °C | 485 - 530 °F | Processing Temperature | |
| Drying Temperature | 79.4 °C | 175 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Suggested Moisture, max | 0.2 | |
| Suggested Regrind, max | 25 |
Users viewing this material also viewed the following:
- Polimeri Europa Europrene® N OZO 7033 NBR-PVC blend
- Parker Chomerics WIN-SHIELD® AgF8 Conductive Film
- Abatron AboCast 8-8/Abocure 8-8 Epoxy (discontinued **)
- SABIC Innovative Plastics LNP LUBRICOMP QCL349 PA 6/10 (Asia Pacific)
- SABIC Innovative Plastics LNP LUBRICOMP WX95752L PBT
- Solvay Specialty Polymers Solef® 1006 Polyvinylidene Fluoride (PVDF)
- STAR Thermoplastic Alloys & Rubbers StarCLEAR CLR-1030 TPE
- 3M 4085 Double Coated Urethane Foam Tape
- ChevronTexaco Pinnacle® EP 680
- Teknor Apex Monprene® MP-1875HF Thermoplastic Elastomer
Copyright © lookpolymers.com All Rights Reserved