Technetics Group Amicon™ PEEK 30% Glass Filled (Unverified Data**)
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Technetics Group Amicon™ PEEK 30% Glass Filled
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Technetics Group (formerly Plastomer Technologies)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.51 g/cc | 1.51 g/cc | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | 24 hours; ASTM D570 (2) |
| Water Absorption at Saturation | 0.30 % | 0.30 % | ASTM D570 (2) |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 86 | 86 | ASTM D2240 |
| Tensile Strength, Ultimate | 103 MPa | 15000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Modulus of Elasticity | 6.21 GPa | 900 ksi | ASTM D638 |
| Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
| Flexural Modulus | 6.89 GPa | 1000 ksi | ASTM D790 |
| Compressive Strength | 179 MPa | 26000 psi | ASTM D695 |
| Izod Impact, Notched | 0.747 J/cm | 1.40 ft-lb/in | ASTM D256 type "A" |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 21.6 µm/m-°C @Temperature 100 °C |
12.0 µin/in-°F @Temperature 212 °F |
ASTM E-831 (TMA) |
| Maximum Service Temperature, Air | 249 °C | 480 °F | |
| Flammability, UL94 | V-0 @Thickness 3.17 mm |
V-0 @Thickness 0.125 in |
ASTM UL-94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | ASTM D149 |
Users viewing this material also viewed the following:
- MV Labs MN200 MnBr2·4H2O Manganese(II) bromide tetrahydrate
- Magyar Aluminum ALO-P54 Alumina
- Mikro-Technik 8036 R/U Carboxymethylcellulose (CMC)
- A. Schulman POLYBATCH™ White 8153/UV2 Concentrate Based In Polyethylene
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 3 PHR Di-Cup 40C
- CP-Polymer-Technik Wellamid® 6000 HWUVCP Nylon 6, UV Stabilized, Heat Stabilized, Dry
- Fainplast Compounds CKL 59/OP Flexible PVC, Sheathing Lead Free
- Ametek Tungsten-Copper Composites AWC 8515
- SABIC Innovative Plastics Xenoy® XD1647 PBT+PC (Europe-Africa-Middle East)
- DuPont Performance Polymers Hypalon® 30 Chlorosulfonated Polyethylene Rubber, Gum Compound (discontinued **)&
Copyright © lookpolymers.com All Rights Reserved