Techmer ES Plastiblend® ABS 7000
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | Techmer ES |
| Trade Name | Plastiblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Plastiblend® ABS 7000.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFeatures: Low GlossInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm @Thickness 3.17 mm |
0.0060 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 6.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
6.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 90 | 90 | ASTM D785 |
| Tensile Strength, Yield | 35.2 MPa | 5100 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Flexural Strength | 60.7 MPa | 8800 psi | ASTM D790 |
| Flexural Modulus | 2.07 GPa | 300 ksi | ASTM D790 |
| Izod Impact, Notched | 2.67 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
5.00 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| 3.74 J/cm @Thickness 3.17 mm, Temperature 0.000 °C |
7.00 ft-lb/in @Thickness 0.125 in, Temperature 32.0 °F |
ASTM D256 | |
| 3.74 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
7.00 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 88.9 °C | 192 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.2 °C | 180 °F | Unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- MV Labs ND100 Nd(C2H3O2)3·xH2O Neodymium acetate hydrate
- Rogers Corporation Poron® ThinStik™ 92-09020 Self-Adhesive Urethane Foam
- Karina E CAK 60-48/1-F Black PVC Compound
- Momentive Performance Materials HBR Hot-Pressed Boron Nitride
- SABIC Innovative Plastics LNP STAT-KON DE0029 PC
- Techmer ES HiFill® HIPS TM40 WT 40% Talc Filled
- A. Schulman LP554-01 Narrow Molecular Weight Homopolymer, High-Density Polyethylene
- Epoxy Technology EPO-TEK® H20S Electrically Conductive, Silver Epoxy for Die Stamping
- 3M Scotchcal™ ElectroCut™ 7125-139 Graphic Film
Copyright © lookpolymers.com All Rights Reserved