Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), PTFE/Glass-Fiber Filled |
Manufacturer | Techmer ES |
Trade Name | Luriblend® |
Port | Ningbo port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Techmer ES Luriblend® PPS GF30 TL15 30% Glass Filled.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.68 g/cc | 0.0607 lb/in³ | ASTM D792 |
Water Absorption | 0.030 % @Time 86400 sec |
0.030 % @Time 24.0 hour |
ASTM D570 |
Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 3.17 mm |
0.0020 in/in @Thickness 0.125 in |
ASTM D955 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Hardness, Rockwell R | 121 | 121 | ASTM D785 |
Tensile Strength, Yield | 132 MPa | 19200 psi | ASTM D638 |
Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
Flexural Yield Strength | 171 MPa | 24800 psi | ASTM D790 |
Flexural Modulus | 10.0 GPa | 1450 ksi | ASTM D790 |
Izod Impact, Notched | 0.694 J/cm @Thickness 3.17 mm |
1.30 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Parallel to Flow | 27.0 µm/m-°C | 15.0 µin/in-°F | ASTM D696 |
Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | Unannealed; ASTM D648 |
Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | Unannealed; ASTM D648 |
Flammability, UL94 | V-0 | V-0 |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 |
Dielectric Strength | 19.7 kV/mm | 500 kV/in | Method A (Short-Time); ASTM D149 |