Techmer ES Luriblend® PE 5902
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE |
| Manufacturer | Techmer ES |
| Trade Name | Luriblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Luriblend® PE 5902.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsAdditive: LubricantFeatures: Lubricated, Good Wear Resistance and Low FrictionProcessing Method: Injection MoldingInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.970 g/cc | 0.0350 lb/in³ | ASTM D792 |
| Water Absorption | 0.070 % @Time 86400 sec |
0.070 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.030 cm/cm @Thickness 3.17 mm |
0.030 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 1.0 g/10 min @Load 10.0 kg, Temperature 190 °C |
1.0 g/10 min @Load 22.0 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 25.5 MPa | 3700 psi | ASTM D638 |
| Elongation at Break | 30 % | 30 % | ASTM D638 |
| Flexural Strength | 41.4 MPa | 6000 psi | ASTM D790 |
| Flexural Modulus | 0.483 GPa | 70.0 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm |
2.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Coefficient of Friction, Dynamic | 0.15 | 0.15 | ASTM D1894 |
| Coefficient of Friction, Static | 0.080 | 0.080 | ASTM D1894 |
| K (wear) Factor | 32.2 x 10-8 mm³/N-M | 16.0 x 10-10 in³-min/ft-lb-hr | |
| Limiting Pressure Velocity | 0.350 MPa-m/sec | 10000 psi-ft/min | 10 fpm |
| 0.631 MPa-m/sec | 18000 psi-ft/min | 100 fpm | |
| 0.683 MPa-m/sec | 19500 psi-ft/min | 1000 fpm |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 93.3 °C | 200 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 54.4 °C | 130 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Solvay Chemicals Calcium fluoride
- Polyram PlusTek PA201 Nylon 66 for Extrusion
- Wieland Porta OP M-1 Solder
- Zeon Chemicals Nipol® 1472X Nitrile Powder and Crumb Elastomer
- Chosun Refractories AH-5 Acid-Proof and Heat-Resistant Brick
- Dow C7014-35RNA Polypropylene Impact Copolymer Resin
- ConocoPhillips ANDEROL® FGC 150 Compressor Fluid, Synthetic Food Grade ISO 150
- Asahi Kasei Thermofil P-9900-1760 Unreinforced, Heat Stabilized, Impact Modified
- Loctite® CHIPBONDER® 3619 Low Temperature Cure, Syringe Dispense
- ExxonMobil Escorene® LD-332 EVA Packaging Film Resin, High Clarity (discontinued **)
Copyright © lookpolymers.com All Rights Reserved