Techmer ES HiFill® PP GB30 30% Glass Beads Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Glass Bead Filled |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® PP GB30 30% Glass Beads Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Bead, 30% Filler by WeightInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ASTM D792 |
| Water Absorption | 0.020 % @Time 86400 sec |
0.020 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.017 cm/cm @Thickness 3.17 mm |
0.017 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 97 | 97 | ASTM D785 |
| Tensile Strength, Yield | 23.4 MPa | 3400 psi | ASTM D638 |
| Elongation at Yield | 9.0 % | 9.0 % | ASTM D638 |
| Flexural Yield Strength | 32.4 MPa | 4700 psi | ASTM D790 |
| Flexural Modulus | 1.86 GPa | 270 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm @Thickness 3.17 mm |
0.600 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 64.8 µm/m-°C | 36.0 µin/in-°F | ASTM D696 |
| Melting Point | 170 °C | 338 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 116 °C | 240 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 68.3 °C | 155 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible A7000 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Abatron AboCast 1 A/B Filled Potting Compound (discontinued **)
- SABIC Innovative Plastics LNP Lubricomp RFL38 PA 66 (Europe-Africa-Middle East)
- A. Schulman POLYFORT™ FXP 2600-3120 CaC02 Filled Homopolymer Polypropylene
- A. Schulman PP 3491 Polypropylene Homopolymer Polypropylene
- Alcoa Toolrite 2011®-T8 Aluminum
- 3M 101+ Value Masking Tape
- Arlon E950-10RXX-M8 0.050" (1.27 mm) Cured Silicone Rubber with PSA liner
- 3M Scotchcal™ ElectroCut™ 7125-103 Graphic Film
- BASF Ultramid® SEG7 35% Glass Filled PA6 (Dry)
Copyright © lookpolymers.com All Rights Reserved