Techmer ES HiFill® HIPS TM10 WT155 10% Talc Filled
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® HIPS TM10 WT155 10% Talc Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Talc Filler, 10% Filler by WeightAppearance: WhiteInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ASTM D792 |
| Melt Flow | 6.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 22.8 MPa | 3300 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Flexural Strength | 35.9 MPa | 5200 psi | ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm |
2.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 7.20 µm/m-°C | 4.00 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | ASTM D257 |
| Dielectric Strength | 18.1 kV/mm | 460 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- MV Labs ER500 ErF3 Erbium fluoride
- Polymer Resources TP-FR-IM Polybutylene Terephthalate, Impact Modified, Flame Retardant, Low Flow
- 3M Dyneon™ TFM™ 1605 Modified PTFE Powder (discontinued **)
- SABIC Innovative Plastics LNP Thermocomp RF00AES PA 66 (Europe-Africa-Middle East)
- A. Schulman POLYBATCH™ Cedar 10310U Concentrate Based In LLDPE
- Daikin NEOFLON ND-1 FEP Dispersion, Translucent White
- COI Ceramics Al2O3SiO2 Oxide Hollow Spheres
- Teknor Apex APEX® 3201-75 Polyvinyl Chloride, Flexible
- Pau Tai Unistab BZ-695F Mixed Metal Liquid Stabilizer for PVC Barium/Zinc Self-Lubricating
Copyright © lookpolymers.com All Rights Reserved