Techmer ES HiFill FR® PPO/HIPS MM20 FR 20% Mineral Filled
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) , Polystyrene + Polyphenylene Ether, Glass + Mineral Filler |
| Manufacturer | Techmer ES |
| Trade Name | HiFill FR® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill FR® PPO/HIPS MM20 FR 20% Mineral Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Mineral Filler, 20% Filler by Weight Features: Flame RetardantInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D792 |
| Water Absorption | 0.060 % @Time 86400 sec |
0.060 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm @Thickness 3.17 mm |
0.0060 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 106 | 106 | ASTM D785 |
| Tensile Strength, Yield | 75.8 MPa | 11000 psi | ASTM D638 |
| Elongation at Break | 20 % | 20 % | ASTM D638 |
| Flexural Yield Strength | 117 MPa | 17000 psi | ASTM D790 |
| Flexural Modulus | 3.52 GPa | 510 ksi | ASTM D790 |
| Izod Impact, Notched | 1.28 J/cm @Thickness 3.17 mm |
2.40 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 36.0 µm/m-°C | 20.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 126 °C | 259 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 116 °C | 240 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 |
| Dielectric Strength | 17.3 kV/mm | 440 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Omya TITAN® 200 - LU Calcium Carbonate
- SABIC Innovative Plastics Cycoloy® IP1000 PC+ABS (Asia Pacific)
- Polymax® Maxelast® P1957TA TPE, PP Overmold or Standalone use
- Chevron Phillips Vytek™ V205C6 Enhanced LLDPE Blown Film Resin (discontinued **)
- SABIC Innovative Plastics Valox® IQ420 PBT
- DuPont Performance Polymers Kalrez® 8002 FFKM Perfluoroelastomer
- ConocoPhillips EP Polyurea NLGI Grade No. 1
- Austin Novel Materials Texalan® 665A Polyester and Polyether based TPU
- Grupo Repol Dinalon® B1X25 HI PA6 High Impact
Copyright © lookpolymers.com All Rights Reserved