- Techmer ES Elastoblend® PA6 GF33 IM3 BK 33% Glass Filled
Techmer ES Elastoblend® PA6 GF33 IM3 BK 33% Glass Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled , Nylon 6, Heat Stabilized , Nylon 6, Impact Grade |
| Manufacturer | Techmer ES |
| Trade Name | Elastoblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Elastoblend® PA6 GF33 IM3 BK 33% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Heat Stabilizer, Impact Modifier and LubricantFeatures: Heat Stabilized, Impact Modified and LubricatedAppearance: BlackInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ASTM D792 |
| Water Absorption | 0.97 % @Time 86400 sec |
0.97 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 3.17 mm |
0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 132 MPa | 19100 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 186 MPa | 27000 psi | ASTM D790 |
| Flexural Modulus | 7.45 GPa | 1080 ksi | ASTM D790 |
| Izod Impact, Notched | 1.01 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
1.90 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 |
| 2.46 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
4.60 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 13.9 J/cm @Thickness 3.17 mm |
26.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 36.0 µm/m-°C | 20.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+13 ohm-cm | 2.00e+13 ohm-cm | ASTM D257 |
| Dielectric Strength | 15.4 kV/mm | 390 kV/in | Method A (Short-Time); ASTM D149 |
Users viewing this material also viewed the following:
- Proto3000 Objet TangoBlackPlus FullCure980 Rubber-like Prototyping Polymer
- Piezo Kinetics 802 Lead Zirconate Titanate Piezoelectric
- Eastman 800A Polyethylene (discontinued **)
- Lucobit Lucofin® 1494H Chemically Modified Polyethylene
- Solvay Specialty Polymers Solef® 60512 Polyvinylidene Fluoride (PVDF)
- Total FE 8004 LDPE blown film
- Arlon 940-15R##-P0 0.040" (1.02 mm) Cured Self-fusing Silicone Tape
- BASF Quadrol® Specialty Polyol
- Solvay Specialty Polymers Mindel® S-1000 Modified Polysulfone (discontinued **)
Copyright © lookpolymers.com All Rights Reserved