TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 3.0 PHR Di-Cup 40C Peroxide, Hardness 66A

Category	Polymer , Thermoset , Polyester, TS , Polyurethane, TS , Thermoset Polyurethane, Elastomer, Unreinforced , Rubber or Thermoset Elastomer (TSE)
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 3.0 PHR Di-Cup 40C Peroxide, Hardness 66A.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Millathane® 76 is a very suitable choice for use in products such as bushings, small copier rolls; automotive applications — bumpers, o-rings, hydraulic seals, belts, gaskets, solid tires — and many other high performance polyurethane applications. Millathane 76 can be vulcanized by sulfur or peroxide cured systems.Curing of Millathane®76 can easily be done with many types of peroxides. Millathane76 peroxide vulcanizates have superior compression set, greater heat stability, and are more resistant to reversion than sulfur cures.FormulationDi-Cup 40C 3.0Millathane 76 100.0Stearic Acid 0.25Poly AC 617A0.5N-55035.0TP-953.0All information provided by TSE Industries

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	66	66
	70	70	heat aged 70 hours @ 100ºC
Tensile Strength, Yield	22.79 MPa	3305 psi
	27.50 MPa	3989 psi	heat aged 70 hours @ 100ºC
Elongation at Yield	256 %	256 %	heat aged 70 hours @ 100ºC
	296 %	296 %
100% Modulus	0.00405 GPa	0.587 ksi
200% Modulus	0.01364 GPa	1.979 ksi
Tear Strength	52.4 kN/m	299 pli	Die C
Compression Set	24 % @Temperature 100 °C, Time 79200 sec	24 % @Temperature 212 °F, Time 22.0 hour

Processing Properties	Metric	English	Comments
Cure Time	5.00 min @Temperature 83.3 °C	0.0833 hour @Temperature 182 °F