Supreme Petrochem SP6415 High Gloss High Impact Polystyrene

Category	Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified
Manufacturer	Supreme Petrochem LTD
Trade Name
Port	Shanghai port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	Supreme Petrochem SP6415 High Gloss High Impact Polystyrene.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Characteristics Very good gloss with the retention of ESCR properties Good toughness Also available in various color shades Processing Injection moldingApplications Refrigerator end caps Refrigerator table tops Material Status: Commercial : ActiveAgency Ratings: FDA 21 CFR 177.1640Information provided by Supreme Petrochem LTD

Physical Properties	Metric	English	Comments
Specific Gravity	1.04 g/cc	1.04 g/cc	ASTM D792
Melt Flow	5.5 g/10 min <br>@Load 5.00 kg,<br> Temperature 200 Â°C	5.5 g/10 min <br>@Load 11.0 lb,<br> Temperature 392 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	24.5 MPa	3550 psi	50 mm/min; ASTM D638
Elongation at Break	30 %	30 %	50 mm/min; ASTM D638
Flexural Strength	44.1 MPa <br>@Thickness 3.20 mm	6400 psi <br>@Thickness 0.126 in	ASTM D790
Flexural Modulus	1.96 GPa <br>@Thickness 3.20 mm	284 ksi <br>@Thickness 0.126 in	ASTM D790
Izod Impact, Notched	1.35 J/cm <br>@Thickness 3.20 mm	2.53 ft-lb/in <br>@Thickness 0.126 in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	78.0 Â°C	172 Â°F	ASTM D648
Vicat Softening Point	99.0 Â°C	210 Â°F	1kg / 120Â°C; ASTM D1525
Flammability, UL94	HB <br>@Thickness 1.50 mm	HB <br>@Thickness 0.0591 in

Optical Properties	Metric	English	Comments
Gloss	90 %	90 %	at 60Â°; ASTM D523

Processing Properties	Metric	English	Comments
Melt Temperature	180 - 260 Â°C	356 - 500 Â°F
Mold Temperature	40.0 - 60.0 Â°C	104 - 140 Â°F