Sumitomo Bakelite Durez® 156 Phenolic, Compression Grade
| Category | Polymer , Thermoset , Phenolic , Phenolic, Novolac, Mineral/Fiber Filled |
| Manufacturer | Sumitomo Bakelite High Peformance Plastics |
| Trade Name | Durez® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sumitomo Bakelite Durez® 156 Phenolic, Compression Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Durez 156 Black Phenolic is a two-stage, asbestos-free, heat resistant/electrical molding material. It exhibits excellent dimensional stability, high heat resistance, good molded appearance, and UL flammability rating. Typical applications include automotive carburetor spacers, sealing rings, thrust washers, speedometer sleeves, appliance terminals, probe controls, insulators, light baffles, etc.Durez 156 is fungus resistant per Mil-E-5272C.Information provided by Sumitomo Bak North America, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | ASTM D792 |
| Apparent Bulk Density | 0.650 g/cc | 0.0235 lb/in³ | ASTM D1895 |
| Water Absorption | 0.30 % | 0.30 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
| Tensile Modulus | 10.3 GPa | 1490 ksi | ASTM D638 |
| Flexural Strength | 72.0 MPa | 10400 psi | |
| Compressive Strength | 196 MPa | 28400 psi | ASTM D695 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 160 °C | 320 °F | UL temperature Index |
| Deflection Temperature at 1.8 MPa (264 psi) | 191 °C | 376 °F | ASTM D648 |
| Flammability, UL94 | V-1 @Thickness 0.500 mm |
V-1 @Thickness 0.0197 in |
|
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D257 |
| Dielectric Constant | 5.0 @Frequency 1e+6 Hz |
5.0 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 10.8 kV/mm | 274 kV/in | Step by step; ASTM D149 |
| 11.8 kV/mm | 300 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.050 @Frequency 1e+6 Hz |
0.050 @Frequency 1e+6 Hz |
ASTM D150 |
| Arc Resistance | 180 sec | 180 sec | ASTM D495 |
| Comparative Tracking Index | 180 V | 180 V | IEC Tracking Index |
Users viewing this material also viewed the following:
- Radici Radiflam® S FR (cond.) Nylon 6
- LATI Latigray 75/4-01 CX/45 PBT
- Sylvin Technologies 8940-95 Natural PVC Extrusion Compound
- Schwartz Technical Plastics LAMIGAMID® 600 Polyoxymethylene
- Techmer ES HiFill® PA6 GF20 RM BK 20% Glass Filled
- Hexcel® Redux® 609 (0.06 psf) Adhesive film for bonding metallic and composite components
- 3M Fluorinert™ FC-72 Electronic Liquid
- Beijing Ranger Chem SM-607R Solid Epoxy Resin
- Karina E 02/242-RG-PO Yellow Color Concentrate for PVC
Copyright © lookpolymers.com All Rights Reserved