- Polycarbonate/ABS Alloy, Unreinforced
- Styron Pulse® 1310 ABS + Polycarbonate
Styron Pulse® 1310 ABS + Polycarbonate
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | Pulse® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron Pulse® 1310 ABS + Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PULSE® 1310 Engineering resin offers a superior total performance with a balance of heat resistance, practical toughness, high and low temperature impact strength retention and ease of processing. PULSE 1310 Engineering resin is UL listed.Data provided by Dow Chemical.This product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ASTM Data |
| Water Absorption | 0.15 % | 0.15 % | |
| Moisture Absorption at Equilibrium | 0.32 % | 0.32 % | Humidity Absorption |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | |
| Melt Flow | 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
5.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM Data |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | |
| Tensile Strength, Ultimate | 48.3 MPa | 7010 psi | ASTM Data |
| Tensile Strength, Yield | 53.1 MPa | 7700 psi | ASTM Data |
| Elongation at Break | 100 % | 100 % | ASTM Data |
| Elongation at Yield | 4.1 % | 4.1 % | ISO Data |
| Tensile Modulus | 2.30 GPa | 334 ksi | ISO Data. |
| Izod Impact, Notched | 5.34 J/cm | 10.0 ft-lb/in | ASTM Data |
| 4.80 J/cm @Temperature -50.0 °C |
8.99 ft-lb/in @Temperature -58.0 °F |
ASTM Data | |
| Charpy Impact Unnotched | NB | NB | ISO Data |
| NB | NB | ISO Data, Low Temp | |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO Data, Low Temp |
| 6.50 J/cm² | 30.9 ft-lb/in² | ISO Data | |
| Impact Test | 56.5 J @Temperature -30.0 °C |
41.7 ft-lb @Temperature -22.0 °F |
Instrumented Dart Total Energy |
| 56.5 J @Temperature 23.0 °C |
41.7 ft-lb @Temperature 73.4 °F |
Instrumented Dart Total Energy |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 73.8 µm/m-°C @Temperature 20.0 °C |
41.0 µin/in-°F @Temperature 68.0 °F |
ASTM data |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.1 °C | 205 °F | Unannealed; 107°C (225°F) annealed; ASTM Data |
| Vicat Softening Point | 137 °C | 279 °F | |
| Flammability, UL94 | HB @Thickness 1.47 mm |
HB @Thickness 0.0579 in |
Users viewing this material also viewed the following:
- P & P Technology Stainless Steel (Alloy 304) Knitted Cored Shielding Mesh
- Nilit FRIANYL A63 CV-CM 0830 9005/Z Powder-coatable nylon 6.6 for injection molding, 8% carbon fiber reinforced, 30% ceramic filled
- Pyrotek Bonded Particle Filtration Media
- PolyOne Geon™ Vinyl Flexible XV3807 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Glastic Laminates/Shapes UTS Fiberglass-Reinforced Polyester Laminate
- Teknor Apex APEX® 3302-75 Polyvinyl Chloride, Flexible
- A. Schulman PP 3487-01 Polypropylene Homopolymer Polypropylene
- Dow PAPI™ 27 Polymeric MDI
- DuPont Performance Polymers Rynite® 415HP NC010 PET (Unverified Data**)
- ConocoPhillips 32 Ultra-Clean Super Hydraulic Oil
Copyright © lookpolymers.com All Rights Reserved