Styrolution Styrolux HS 70 SBC
| Category | Polymer , Thermoplastic , Styrene-Butadiene , Styrene-Butadiene Copolymer, SBC |
| Manufacturer | Styrolution |
| Trade Name | Styrolux |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Styrolux HS 70 SBC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | ISO 1183 |
| Water Absorption | 0.070 % | 0.070 % | ISO 62 |
| Moisture Absorption at Equilibrium | 0.070 % | 0.070 % | 23°C/50% R.H.; ISO 62 |
| Melt Flow | 13 g/10 min @Load 5.00 kg, Temperature 200 °C |
13 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM Test |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 29.0 MPa | 4210 psi | ASTM Data |
| Film Tensile Strength at Yield, TD | 70.0 MPa | 10200 psi | ASTM Data |
| Tensile Strength, Yield | 28.3 MPa | 4100 psi | 2 in/min; ASTM Test |
| Film Elongation at Yield, MD | 400 % | 400 % | ASTM Data |
| Film Elongation at Yield, TD | 110 % | 110 % | ASTM Data |
| Elongation at Break | 40 % | 40 % | 2 in/min; ASTM Test |
| Elongation at Yield | 2.0 % | 2.0 % | 2 in/min; ASTM Test |
| Tensile Modulus | 2.07 GPa | 300 ksi | 2 in/min; ASTM Test |
| Flexural Strength | 27.0 MPa | 3920 psi | ASTM Test |
| Flexural Modulus | 1.39 GPa | 202 ksi | ASTM Test |
| Dart Drop, Total Energy | 4.50 J | 3.32 ft-lb | ASTM Test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM Test |
| Vicat Softening Point | 72.0 °C | 162 °F | Rate "B" Loading 1 (120 degC/h 10N); ASTM Test |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 2.0 % @Thickness 3.20 mm |
2.0 % @Thickness 0.126 in |
ASTM Test |
| Gloss | 140 % | 140 % | 60° Specular; ASTM Test |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 - 230 °C | 356 - 446 °F | Extrusion |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Clear | |
| Commercial Status | Active America | |
| Impact Modified | No | |
| Primary Processing Technique | Extrusion |
Users viewing this material also viewed the following:
- NOVA Chemicals Novapol® HB-W555-A HDPE Blow Molding Resin
- PolyOne Geon™ Vinyl Flexible XV 3432 Trans 9000 Polyvinyl Chloride, Flexible (PVC, Flexible)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 0.0 PHR Caytur 4
- Henkel Turco T-4181L Liquid Alkaline Rust Remover
- Global PP-2300-NC Polypropylene Block Copolymer
- H.C. Starck Amperit® 599.074 Agglomerated Sintered Molybdenum Carbide (Cr2O3)
- Schott SF1 Glass
- Bhansali Engineering Abstron KU-600 ABS Super Heat Resistant
- Arkema Group Evatane® 1005 VN 5 Ethylene Vinyl Acetate
- Addiplast Addilene J 220 M40 Polypropylene Copolymer
Copyright © lookpolymers.com All Rights Reserved