| Category | Polymer , Thermoplastic , Styrene-Butadiene , Styrene-Butadiene Copolymer, SBC |
| Manufacturer | Styrolution |
| Trade Name | Styrolux |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Styrolux BX6400 SBC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Styrolux BX6400 is a developmental styrene butadiene copolymer (SBC) of high clarity and ultimate toughness used mainly in sheet and film extrusion and thermoforming applications. It is specifically designed for improved performance in blends with general-purpose polystyrene, providing parts with an excellent balance of toughness and transparency.Outstanding toughnessHigh GPPS blend capabilityExcellent clarityInformation provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Absorption at Saturation | 0.070 % @Temperature 23.0 °C |
0.070 % @Temperature 73.4 °F |
ISO 62 |
| Melt Flow | 12 g/10 min @Load 5.00 kg, Temperature 200 °C |
12 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 97 | 97 | ISO 868 |
| Hardness, Shore D | 58 | 58 | ISO 868 |
| Tensile Strength, Yield | 15.0 MPa | 2180 psi | ISO 527 |
| Elongation at Break | 300 % | 300 % | ISO 527 |
| Elongation at Yield | 2.0 % | 2.0 % | ISO 527 |
| Tensile Modulus | 0.900 GPa | 131 ksi | ISO 527 |
| Flexural Strength | 18.0 MPa | 2610 psi | ISO 178 |
| Flexural Modulus | 0.900 GPa | 131 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ASTM D 256 | |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 180/A | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179 |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 8.50 J/cm² | 40.4 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 35.0 °C @Load 1.02 kg |
95.0 °F @Load 2.25 lb |
50°C/h; ISO 306 |
| 67.0 °C @Load 5.10 kg |
153 °F @Load 11.2 lb |
50°C/h; ISO 306 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 3.0 % | 3.0 % | ASTM D 1003 |
| Transmission, Visible | >= 89 % @Wavelength 550 nm |
>= 89 % @Wavelength 550 nm |
ASTM D 1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 190 - 230 °C | 374 - 446 °F | ISO 294 |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 20-7796 Polyphthalamide, with aramid reinforcement and PTFE
- Borealis Borcell™ LE1120 Low Density Polyethylene for Physically Foamed Cellular Insulation
- A. Schulman POLYFORT™ FPP 3716 Talc Filled Copolymer Polypropylene
- Hexcel® HexWeb® HRP - 3/8 - 3.2 Fiberglass/Phenolic Honeycomb
- DAK Americas Laser+® HS Ti818 (G51A) PET
- Clariant PA123G20 Nylon 66, 20% Glass Fiber, Impact Modified, Heat Stabilized
- Dymax 930 Coil Terminating, Tamper proofing and Structural Electronic Bonder
Copyright © lookpolymers.com All Rights Reserved