Styrolution Polystyrol 454 C GR 2 PS

Category	Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Molded, Unreinforced
Manufacturer	Styrolution
Trade Name	Polystyrol
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Styrolution Polystyrol 454 C GR 2 PS.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Polystyrol 454 C is an impact resistant polystyrene with a good balance of toughness, high flow, heat resistance and high gloss.Applications: TV-front panels and back covers, VCR fronts, internal parts for refrigerators, office and household articles. Vacuum cleaner housings; toilet flush; telephones; air conditioner housings; toys; Coextruded gloss layers.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS

Physical Properties	Metric	English	Comments
Density	1.022 g/cc	0.03692 lb/inÂ³	ISO 1183
Water Absorption	<= 0.10 %	<= 0.10 %	ISO 62
Moisture Absorption at Equilibrium	<= 0.10 %	<= 0.10 %	23Â°C/50% RH; ISO 62
Melt Flow	14.308 g/10 min @Load 5.00 kg, Temperature 200 Â°C	14.308 g/10 min @Load 11.0 lb, Temperature 392 Â°F	ISO 1133

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	90.0 MPa @Load 36.5 kg, Time 30.0 sec	13100 psi @Load 80.5 lb, Time 0.00833 hour	ISO 2039-1
Tensile Strength, Yield	27.0 MPa	3920 psi	50 mm/min; ISO 527-1/-2
Elongation at Break	25 %	25 %	Nominal, 50mm/min; ISO 527-1/-2
Elongation at Yield	1.4 %	1.4 %	50 mm/min; ISO 527-1/-2
Tensile Modulus	2.20 GPa	319 ksi	ISO 527-1/-2
Flexural Strength	41.0 MPa	5950 psi	ISO 178
Shear Modulus	0.900 GPa	131 ksi	ISO 6721-2
Charpy Impact Unnotched	<= 12.0 J/cmÂ² @Temperature -30.0 Â°C	<= 57.1 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 179/1eU
	<= 15.0 J/cmÂ² @Temperature 23.0 Â°C	<= 71.4 ft-lb/inÂ² @Temperature 73.4 Â°F	ISO 179/1eU
Charpy Impact, Notched	1.60 J/cmÂ²	7.61 ft-lb/inÂ²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	82.0 Â°C	180 Â°F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	78.0 Â°C	172 Â°F	ISO 75-1/-2
Vicat Softening Point	82.0 Â°C	180 Â°F	VST/B/50; ISO 306
	91.0 Â°C	196 Â°F	VST/A/50; ISO 306
Flammability, UL94	HB @Diameter 1.60 mm	HB @Diameter 0.0630 in	IEC 60695-11-10
	HB @Diameter 3.18 mm	HB @Diameter 0.125 in	IEC 60695-11-10

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+16 ohm-cm	>= 1.00e+16 ohm-cm	IEC 60093
Surface Resistance	>= 1.00e+13 ohm	>= 1.00e+13 ohm	IEC 60093
Dielectric Constant	2.5 @Frequency 1.00e+6 Hz	2.5 @Frequency 1.00e+6 Hz	IEC 60250
	2.5 @Frequency 100 Hz	2.5 @Frequency 100 Hz	IEC 60250
Dielectric Strength	160 kV/mm	4060 kV/in	K20/P50; IEC 60243-1

Processing Properties	Metric	English	Comments
Melt Temperature	180 - 260 Â°C	356 - 500 Â°F	Injection Molding
Mold Temperature	10.0 - 60.0 Â°C	50.0 - 140 Â°F	Injection Molding

Descriptive Properties	Value	Comments
Color	Natural
Commercial Status	Europe
Primary Processing Technique	Injection Molding and Extrusion
Surface Gloss	70	Skalenteile