Special Metals NIMONIC® Alloy PE11
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | NIMONIC® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals NIMONIC® Alloy PE11.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A nickel-iron-chromium alloy precipitation hardened by titanium and aluminum and solid-solution strengthened by an addition of molybdenum. It was developed as a high-strength sheet alloy for use at temperatures to 1020°F (550°C). The high iron content provides good workability and also relatively high tensile ductility, especially after welding. Used for components of gas turbines. Standard product forms are round, flats, extruded section, plate, sheet, and wire.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.02 g/cc | 0.290 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 950 MPa @Temperature 650 °C |
138000 psi @Temperature 1200 °F |
Precipitation Hardened prior to test |
| 1060 MPa @Temperature 23.0 °C |
154000 psi @Temperature 73.4 °F |
||
| Tensile Strength, Yield | 700 MPa @Strain 0.200 % |
102000 psi @Strain 0.200 % |
Precipitation Hardened. Value at room temperature |
| 680 MPa @Strain 0.200 %, Temperature 650 °C |
98600 psi @Strain 0.200 %, Temperature 1200 °F |
Precipitation Hardened prior to test | |
| Elongation at Break | 20 % | 20 % | Precipitation Hardened |
| 15 % @Temperature 650 °C |
15 % @Temperature 1200 °F |
Precipitation Hardened prior to test. |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 0.436 J/g-°C | 0.104 BTU/lb-°F | |
| Melting Point | 1280 - 1350 °C | 2340 - 2460 °F | |
| Solidus | 1280 °C | 2340 °F | |
| Liquidus | 1350 °C | 2460 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 0.70 - 1.0 % | 0.70 - 1.0 % | |
| Boron, B | <= 0.0010 % | <= 0.0010 % | |
| Carbon, C | 0.030 - 0.080 % | 0.030 - 0.080 % | |
| Chromium, Cr | 17 - 19 % | 17 - 19 % | |
| Cobalt, Co | <= 1.0 % | <= 1.0 % | |
| Copper, Cu | <= 0.50 % | <= 0.50 % | |
| Iron, Fe | 32 % | 32 % | As remainder |
| Manganese, Mn | <= 0.20 % | <= 0.20 % | |
| Molybdenum, Mo | 4.75 - 5.75 % | 4.75 - 5.75 % | |
| Nickel, Ni | 37 - 41 % | 37 - 41 % | |
| Silicon, Si | <= 0.50 % | <= 0.50 % | |
| Sulfur, S | <= 0.015 % | <= 0.015 % | |
| Titanium, Ti | 2.2 - 2.5 % | 2.2 - 2.5 % | |
| Zirconium, Zr | 0.020 - 0.050 % | 0.020 - 0.050 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Magnetic Permeability | 1.021 | 1.021 | at 300 oersted (23.9 kA/m) |
Users viewing this material also viewed the following:
- RheTech Products T20P100-517UV 20% Talc Reinforced Polypropylene, UV Stabilized, Interior DX9 Black
- SABIC Innovative Plastics Lexan® 513RS PC (Europe-Africa-Middle East)
- Eastman Tenite 105-28 Cellulose Acetate (discontinued **)
- LG Chemical Lupox® SV-1120 General Purpose PBT, Unreinforced, High Molecular Weight, Extrusion
- Haynes Hastelloy® C-22® alloy, 60% cold worked sheet, aged 100 hours at 500°C
- Sibur 140-13P Polyvinyl Chloride (PVC)
- Unifrax Fiberfrax® Washed 707 High Purity High-Index Fiber
- ExxonMobil Mobil 1 10W-30
- Trelleborg Sealing Solutions Turcite® TA Self-Lubricating Thermoplastic Rod
- Dow Corning Q7-9120 Silicone Fluid, 350 CST
Copyright © lookpolymers.com All Rights Reserved