Special Metals INCOLOY® Alloy DS
| Category | Metal , Superalloy , Iron Base |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | INCOLOY® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals INCOLOY® Alloy DS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A nickel-iron-chromium alloy with an addition of silicon. It has good high-temperature strength and excellent resistance to oxidation and carburization. The silicon content makes the alloy resistant to internal oxidation in high-temperature atmospheres that vary between oxidizing and reducing. Used in industrial furnaces and for heat-treating baskets, trays, and fixtures. Standard product forms are round, plate, sheet, strip, tube, pipe, and wire.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.86 g/cc | 0.284 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 500 MPa @Temperature 425 °C |
72500 psi @Temperature 797 °F |
Solution Annealed prior to test |
| 580 MPa @Temperature 23.0 °C |
84100 psi @Temperature 73.4 °F |
||
| Tensile Strength, Yield | 215 MPa @Strain 0.200 % |
31200 psi @Strain 0.200 % |
Precipitation Hardened. Value at room temperature |
| 120 MPa @Strain 0.200 %, Temperature 425 °C |
17400 psi @Strain 0.200 %, Temperature 797 °F |
Precipitation Hardened prior to test | |
| Elongation at Break | 60 % | 60 % | Solution Annealed |
| 64 % @Temperature 425 °C |
64 % @Temperature 797 °F |
Solution Annealed prior to test. |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 15.0 µm/m-°C @Temperature 20.0 - 100 °C |
8.33 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Specific Heat Capacity | 0.452 J/g-°C | 0.108 BTU/lb-°F | |
| Thermal Conductivity | 12.0 W/m-K | 83.3 BTU-in/hr-ft²-°F | |
| Melting Point | 1330 - 1400 °C | 2430 - 2550 °F | |
| Solidus | 1330 °C | 2430 °F | |
| Liquidus | 1400 °C | 2550 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.10 % | <= 0.10 % | |
| Chromium, Cr | 17 - 19 % | 17 - 19 % | |
| Copper, Cu | <= 0.50 % | <= 0.50 % | |
| Iron, Fe | 40 % | 40 % | As remainder |
| Manganese, Mn | 0.80 - 1.5 % | 0.80 - 1.5 % | |
| Nickel, Ni | 34.5 - 41 % | 34.5 - 41 % | Including Cobalt |
| Silicon, Si | 1.9 - 2.6 % | 1.9 - 2.6 % | |
| Sulfur, S | <= 0.030 % | <= 0.030 % | |
| Titanium, Ti | <= 0.20 % | <= 0.20 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000108 ohm-cm | 0.000108 ohm-cm | |
| Magnetic Permeability | 1.038 | 1.038 | at 200 oersted (15.9 kA/m) |
Users viewing this material also viewed the following:
- Park Electrochemical Nelcote® E-746 Epoxy Prepreg, 3k 5HS Carbon Reinforced
- Pasargad Polymer Peyvand Pasalen 3P-H3120B Polypropylene, 20% Glass Fiber Reinforced
- KaMin KaMin® 90B Kaolin Clay - Waterwashed
- H.C. Starck Amperit® 558.088 Tungsten Carbide-Cobalt-Chromium 86-10-4 (WC-Co-Cr)
- Polyram RamTal PM3009G5 Acetal, 25% Glass Fiber
- Total PPR 7525MZ Polypropylene, Injection Molding Grade
- Polyram PlusTek PB318G9 Nylon 6 for Injection Molding, 45% Glass-fiber Reinforced, UV Stabilized
- DuPont Teijin Films Mylar® A Polyester Film, 750 Gauge
Copyright © lookpolymers.com All Rights Reserved