Spartech PP5340 Mica Reinforced Homopolymer
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 40% Mica Filler |
| Manufacturer | Spartech |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Spartech PP5340 Mica Reinforced Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Spartech
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc @Temperature 22.8 °C |
1.24 g/cc @Temperature 73.0 °F |
ASTM D792 |
| Filler Content | 40 % | 40 % | Mica |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | 0.125inch wall |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Modulus | 3.03 GPa | 440 ksi | secant; ASTM D790 |
| 4.00 GPa | 580 ksi | tangent; ASTM D790 | |
| Izod Impact, Notched | 0.267 J/cm @Temperature 22.8 °C |
0.500 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 138 °C | 280 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.2 °C | 180 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Polykemi AB SCANMID 6 B12^ F20 Nylon 6, Glass Fiber Reinforced
- PTS POM-90 9.0 MFI Acetal Copolymer
- Kuraray HYBRAR® SC1
- DuPont Teijin Films Mylar® EL Polyester Film, 300 Gauge
- CMT Materials HYTAC® XTL Tough Thermoplastic Syntactic Foam
- Adell DR-16 30% Glass Reinforced Polycarbonate
- SABIC Innovative Plastics Lexan® LX2801 PC (Asia Pacific)
- Shandong Dongyue Polymer DF-101 PTFE Molding Powder (Medium Particle Size)
Copyright © lookpolymers.com All Rights Reserved