- Polyvinylidinefluoride (PVDF), Molded/Extruded
- Solvay Specialty Polymers Solef® 60512/0550 and 60512/0150 Polyvinylidene Fluoride (PVDF)
Solvay Specialty Polymers Solef® 60512/0550 and 60512/0150 Polyvinylidene Fluoride (PVDF)
| Category | Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Solef® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Solef® 60512/0550 and 60512/0150 Polyvinylidene Fluoride (PVDF).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Solef® 60512/0550 and Solef® 60512/0150 are PVDF grades compounded with PTFE for extrusion of anti-wear tapes.Features: CopolymerUses: TapeAdditional Properties: Crystallization Heat - ASTM D3417 38.0 to 48.0 J/g; Heat of Fusion - ASTM D3417 41.0 to 50.0 J/gInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.80 - 1.82 g/cc | 0.0650 - 0.0658 lb/in³ | ISO 1183 |
| Water Absorption | <= 0.040 % @Time 86400 sec |
<= 0.040 % @Time 24.0 hour |
ISO 62 |
| Melt Flow | 2.0 - 4.5 g/10 min @Load 10.0 kg, Temperature 230 °C |
2.0 - 4.5 g/10 min @Load 22.0 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 30.0 - 40.0 MPa @Thickness 1.50 mm |
4350 - 5800 psi @Thickness 0.0591 in |
50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 30.0 - 40.0 MPa @Thickness 1.50 mm |
4350 - 5800 psi @Thickness 0.0591 in |
50 mm/min; ASTM D638 |
| Elongation at Break | 50 - 300 % | 50 - 300 % | 50 mm/min; ASTM D638 |
| Elongation at Yield | 8.0 - 12 % | 8.0 - 12 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 1.10 - 1.35 GPa @Thickness 1.50 mm |
160 - 196 ksi @Thickness 0.0591 in |
1.0 mm/min; ASTM D638 |
| Coefficient of Friction, Dynamic | 0.10 - 0.20 | 0.10 - 0.20 | vs. Itself; ASTM D1894 |
| Coefficient of Friction, Static | 0.050 - 0.20 | 0.050 - 0.20 | vs. Itself; ASTM D1894 |
| Taber Abrasion, mg/1000 Cycles | 5.0 - 10 | 5.0 - 10 | CS-10 Wheel, 1000 g; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 170 - 174 °C | 338 - 345 °F | DSC |
| Crystallization Temperature | 144 - 148 °C | 291 - 298 °F | Peak; ASTM D3418 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America |
Users viewing this material also viewed the following:
- Precision Polymer Engineering N70F Nitrile Rubber
- Teknor Apex APEX® 3201-70 Polyvinyl Chloride, Flexible
- SABIC Innovative Plastics NORYL GTX GTX944 PPE+PA (Asia Pacific)
- Borealis Visico™ LE4423/LE4437 Scorch Retardant, Moisture-Crosslinking Polyethylene Compound for Low Voltage Installation
- A. Schulman INVISION™ VX-5085UI Soft Touch Polyolefin Thermoplastic
- Chosun Refractories APN-1 Special brick
- 3M Bumpon™ SJ5832 Resilient Rollstock
- BASF Lupranate® 5090 Isocyanate
- BASF Neopolen® P 9230 A 0.05 g/cc Core density; Expanded Polypropylene (Europe)
Copyright © lookpolymers.com All Rights Reserved