- Solvay Specialty Polymers Solef® 1015 Polyvinylidene Fluoride (PVDF) (Unverified Data**)
Solvay Specialty Polymers Solef® 1015 Polyvinylidene Fluoride (PVDF) (Unverified Data**)
| Category | Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Solef® 1015 Polyvinylidene Fluoride (PVDF)
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Solef® 1015 PVDF homopolymer has very high viscosity, suitable for membrane manufacturing. It is available exclusively as powder.Information provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.75 - 1.80 g/cc | 1.75 - 1.80 g/cc | ASTM D792 |
| Water Absorption | <= 0.040 % @Temperature 23.0 °C, Time 86400 sec |
<= 0.040 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Melt Flow | 2.8 - 4.6 g/10 min @Load 21.6 kg, Temperature 230 °C |
2.8 - 4.6 g/10 min @Load 47.6 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 35.0 - 50.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C |
5080 - 7250 psi @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 53.0 - 57.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C |
7690 - 8270 psi @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
| Elongation at Break | 20 - 50 % @Thickness 2.00 mm, Temperature 23.0 °C |
20 - 50 % @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
| Elongation at Yield | 5.0 - 10 % @Thickness 2.00 mm, Temperature 23.0 °C |
5.0 - 10 % @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
| Tensile Modulus | 2.10 - 2.30 GPa @Thickness 2.00 mm, Temperature 23.0 °C |
305 - 334 ksi @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 1.0 mm/min; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Heat of Fusion | 50.0 - 56.0 J/g | 21.5 - 24.1 BTU/lb | Crystallization Heat; ASTM D3417 |
| 57.0 - 66.0 J/g | 24.5 - 28.4 BTU/lb | ASTM D3417 | |
| Melting Point | 171 - 175 °C | 340 - 347 °F | ASTM D3418 |
| Crystallization Temperature | 137 - 144 °C | 279 - 291 °F | Peak, DSC; ASTM D3418 |
| Glass Transition Temp, Tg | -40.0 °C | -40.0 °F | ASTM D4065 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Features | Homopolymer | |
| Very high Viscosity | ||
| Forms | Powder | |
| Generic | PVDF | |
| Uses | Membranes |
Users viewing this material also viewed the following:
- Eastman M3007-P Polyethylene (discontinued **)
- Solvay TECHNYL® B 218L V20 Black 44 N PA66, 25% glass fiber, Conditioned
- Samyang Trirex® 3017IR Polycarbonate with Heat Stabilizer
- Dow Corning FOX® PMCP22 Flowable Oxide
- BASF Ultramid® A3HG7 35% Glass Filled PA66 (Conditioned)
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 2.0 PHR MBT
- E-Polymers SEPAZ® LB50 PA6 LFT Resin
- DuPont™ Sclairfilm® BL-1 LLDPE Film, PVDC Coated, 51 µm Thickness (discontinued **)
Copyright © lookpolymers.com All Rights Reserved