- Solvay Specialty Polymers Polidan® T/A-SP Polyethylene, Crosslinked (XLPE)
Solvay Specialty Polymers Polidan® T/A-SP Polyethylene, Crosslinked (XLPE)
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Crosslinkable |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Polidan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Polidan® T/A-SP Polyethylene, Crosslinked (XLPE).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
POLIDAN® T/A-SP is a silane crosslinkable PE compound which is used together with a catalyst masterbatch to accelerate the crosslinking reaction. It is used for flexible crosslinkable pipes.Features: Crosslinkable; Good Processing Stability; High DensityUses: Piping; Plumbing Parts; Potable Water ApplicationsAdditional Properties: Extruder Screw Compression Ratio - >2.5:1; Extruder Screw L/D Ratio - 25:1 to 30:1; Gel Content - EN 579 > 65 %; Head Temperature - 200 °CInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.951 g/cc | 0.0344 lb/in³ | ASTM D792 |
| Melt Flow | 0.60 g/10 min | 0.60 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | >= 20.0 MPa | >= 2900 psi | ASTM D638 |
| Elongation at Break | >= 400 % | >= 400 % | ASTM D638 |
| Tensile Modulus | 0.670 GPa | 97.2 ksi | ISO 527-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 160 µm/m-°C @Temperature 20.0 °C |
88.9 µin/in-°F @Temperature 68.0 °F |
1 |
| Specific Heat Capacity | 1.80 J/g-°C | 0.430 BTU/lb-°F | ASTM C351 |
| Thermal Conductivity | 0.470 - 0.490 W/m-K | 3.26 - 3.40 BTU-in/hr-ft²-°F | ASTM C177 |
| Vicat Softening Point | 127 °C | 261 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 150 - 200 °C | 302 - 392 °F | |
| Zone 2 | 150 - 200 °C | 302 - 392 °F | |
| Zone 3 | 150 - 200 °C | 302 - 392 °F | |
| Zone 4 | 150 - 200 °C | 302 - 392 °F | |
| Zone 5 | 150 - 200 °C | 302 - 392 °F | |
| Die Cooling Temperature | 210 °C | 410 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Agency Ratings | ISO 15875 /2 | |
| Availability | Asia Pacific | |
| Europe | ||
| North America | ||
| Processing Technique | Extrusion; Pipe Extrusion |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 50-7224/V0 Polycarbonate, with glass fiber and PTFE
- Kinlead HSS11 Normal Grade Heat Sealable Film (thickness: 30 µm)
- Lotte Chemical Titan TITANPRO® PM655 Polypropylene homopolymer
- SK Chemicals SKYTHANE® 470A T series Polyurethane
- A. Schulman POLYBATCH™ Orange 10334 Concentrate Based In LLDPE
- Eastman Tenite Butyrate 530E3720010 Clear, Trsp Cellulose Acetate Butyrate
- Haynes 25 alloy, room temperature after 15% cold reduction, 1175°C anneal for 5 minutes
- H.C. Starck Amperit® 529.074 Tungsten Carbide - Hastalloy C 85-15 (NiMoCrFeCo)
- SABIC Innovative Plastics LNP STAT-KON QD000I PA 6/10 (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved