Solvay Specialty Polymers Lavanta® 5115 WH 251 Polyester, High Performance (HPP), 15% Glass Fiber
| Category | Polymer , Thermoplastic , Polyester, TP |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Lavanta® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Lavanta® 5115 WH 251 Polyester, High Performance (HPP), 15% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lavanta® 5115 WH 251 is a high-performance polyester (HPP) is a 15% glass reinforced, injection molding grade developed specifically for HB LED packaging applications that utilize surface mount technology. Lavanta® 5115 WH 251 has high reflectivity with excellent whiteness retention even after thermal and light aging. This gives it excellent reliability for LEDs that operate at high junction temperatures. Features: Fast Molding Cycle; Good Chemical Resistance; Good Color Stability; High Reflectivity; High Stiffness; Light Stabilized; Low Moisture AbsorptionUses: LEDsAdditional Properties: Optical Reflectivity - ASTM E1331 > 95 %; Optical Reflectivity - ASTM E1331 > 95 %; Optical Reflectivity - ASTM E1331 > 96 %Information provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in³ | ISO 1183 |
| Filler Content | 15 % | 15 % | Glass Fiber |
| Water Absorption | 0.050 % @Time 86400 sec |
0.050 % @Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0052 cm/cm | 0.0052 in/in | |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 72.0 MPa | 10400 psi | ASTM D638 |
| Elongation at Break | 1.4 % | 1.4 % | ISO 527-2 |
| Tensile Modulus | 6.82 GPa | 989 ksi | ISO 527-2 |
| Flexural Strength | 110 MPa | 16000 psi | ISO 178 |
| Flexural Modulus | 6.38 GPa | 925 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 2.10 kJ/m² | 0.999 ft-lb/in² | Type 1, Notch A; ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 22.0 µm/m-°C @Temperature 200 - 250 °C |
12.2 µin/in-°F @Temperature 392 - 482 °F |
4 |
| 24.0 µm/m-°C @Temperature 150 - 200 °C |
13.3 µin/in-°F @Temperature 302 - 392 °F |
4 | |
| 26.0 µm/m-°C @Temperature 100 - 150 °C |
14.4 µin/in-°F @Temperature 212 - 302 °F |
4 | |
| 29.0 µm/m-°C @Temperature 50.0 - 100 °C |
16.1 µin/in-°F @Temperature 122 - 212 °F |
4 | |
| CTE, linear, Transverse to Flow | 64.0 µm/m-°C @Temperature 50.0 - 100 °C |
35.6 µin/in-°F @Temperature 122 - 212 °F |
TMA; ASTM E831 |
| 100 µm/m-°C @Temperature 100 - 150 °C |
55.6 µin/in-°F @Temperature 212 - 302 °F |
TMA; ASTM E831 | |
| 130 µm/m-°C @Temperature 150 - 200 °C |
72.2 µin/in-°F @Temperature 302 - 392 °F |
TMA; ASTM E831 | |
| 140 µm/m-°C @Temperature 200 - 250 °C |
77.8 µin/in-°F @Temperature 392 - 482 °F |
TMA; ASTM E831 | |
| Melting Point | 285 °C | 545 °F | ISO 11357-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 267 °C | 513 °F | HDT B; Unannealed; ISO 75-2/B |
| Deflection Temperature at 1.8 MPa (264 psi) | 203 °C | 397 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 305 °C | 581 °F | |
| Front Barrel Temperature | 290 °C | 554 °F | |
| Melt Temperature | 295 - 310 °C | 563 - 590 °F | |
| Mold Temperature | 130 - 150 °C | 266 - 302 °F | |
| Drying Temperature | 120 °C @Time 14400 sec |
248 °F @Time 4.00 hour |
|
| Moisture Content | <= 0.030 % | <= 0.030 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | White | |
| Form | Pellets | |
| Processing Technique | Injection Molding |
Users viewing this material also viewed the following:
- Resinlab® CYNERGY CA6302 Adhesive
- Hexion Bakelite™ PF 12404 Phenolic Formaldehyde Resin, High Surface Quality, Low Shrinkage (discontinued **)&
- H.C. Starck Amperit® 250.071 Water Atomized (NiCr 80-20)
- Lucent Polymers CPP-340 Polypropylene, 40% Calcium Carbonate Filled, Impact Modified
- Lehmann & Voss LUVOCOM® 1800-7432 PET, with PTFE
- Wingate Alloys Winco-Tuf 40 High Strength Wear Plate
- Elektro-Isola G-Etronax PI Polyimide, Glass Fabric Reinforcement, Dark Brown, Tubes
- Eurostar Starflam PX06009 PA6, Glass Fiber Filled, Flame Retardant, Injection Molded
- Chang Chun Plastic Longlite PM T357 Electrical Phenolic Molding Compound
- Bhansali Engineering Abstron IM-29 ABS Injection Molding Grade
Copyright © lookpolymers.com All Rights Reserved