Solvay Specialty Polymers AcudelÂ® 22000 Polyphenylsulfone, Modified (PPSU, Modified)

Category	Polymer , Thermoplastic , Polyphenylsulfone (PPSU)
Manufacturer	Solvay Specialty Polymers
Trade Name	Acudel®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Solvay Specialty Polymers AcudelÂ® 22000 Polyphenylsulfone, Modified (PPSU, Modified).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

AcudelÂ® 22000 is a modified polyphenylsulfone. It is a high-heat, high-performance resin formulation exhibiting very good hydrolytic stability, excellent resistance to acids and bases and good resistance to stress cracking under a broad range of chemical environments. In addition, AcudelÂ® 22000 resin exhibits robust toughness and improved notch resistance compared to both UdelÂ® polysulfone and VeradelÂ® polyethersulfone, although slightly lower than that of neat RadelÂ® polyphenylsulfone. In general, the performance profile of AcudelÂ® 22000 resin falls between polysulfone and polyphenylsulfone.Features: Acid Resistant; Base Resistant; Flame Retardant; Good Chemical Resistance; Good Thermal Stability; Good Toughness; High ESCR (Stress Crack Resist.); High Heat Resistance; Hydrolytically StableUses: Connectors; Fittings; Piping; Plumbing PartsAdditional Properties: Water Absorption - ASTM D570 0.90 %Automotive Specifications ASTM D6394 SP0000A21640; ASTM D6394 SP0412Information provided by Solvay Specialty Polymers.

Physical Properties	Metric	English	Comments
Density	1.28 g/cc	0.0462 lb/inÂ³	ASTM D792
Water Absorption	0.30 % @Time 86400 sec	0.30 % @Time 24.0 hour	ISO 62
Linear Mold Shrinkage, Flow	0.0070 cm/cm	0.0070 in/in
Melt Flow	12 g/10 min @Load 2.16 kg, Temperature 380 Â°C	12 g/10 min @Load 4.76 lb, Temperature 716 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength	77.2 MPa	11200 psi	ASTM D638
Elongation at Break	50 %	50 %	ASTM D638
Elongation at Yield	6.7 %	6.7 %	ASTM D638
Tensile Modulus	2.69 GPa	390 ksi	ASTM D638
Flexural Yield Strength	108 MPa	15700 psi	ASTM D790
Flexural Modulus	2.76 GPa	400 ksi	ASTM D790
Izod Impact, Notched	1.10 J/cm	2.06 ft-lb/in	ASTM D256
Tensile Impact Strength	368 kJ/mÂ²	175 ft-lb/inÂ²	ASTM D1822

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	197 Â°C @Thickness 3.20 mm	387 Â°F @Thickness 0.126 in	Annealed; ASTM D648

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 9.00e+15 ohm-cm	>= 9.00e+15 ohm-cm	ASTM D257
Dielectric Constant	3.4 @Frequency 1.00e+6 Hz	3.4 @Frequency 1.00e+6 Hz	ASTM D150
Dielectric Strength	19.0 kV/mm @Thickness 3.20 mm	483 kV/in @Thickness 0.126 in	ASTM D149
Dissipation Factor	0.0080 @Frequency 1.00e+6 Hz	0.0080 @Frequency 1.00e+6 Hz	ASTM D150

Compliance Properties	Metric	English	Comments
NSF	Yes	Yes	NSF 51; NSF 61

Processing Properties	Metric	English
Melt Temperature	360 - 391 Â°C	680 - 736 Â°F
Mold Temperature	138 - 163 Â°C	280 - 325 Â°F
Drying Temperature	177 Â°C @Time 9000 sec	351 Â°F @Time 2.50 hour

Descriptive Properties	Value	Comments
Agency Ratings	NSF 51; NSF 61
Availability	Asia Pacific
	Europe
	Latin America
	North America
Color	Black; Colors; Light Beige
Form	Pellets
Injection Rate	Fast
Processing Technique	Injection Molding
RoHS Compliance	RoHS Compliant
Screw Compression Ratio	2.2:1.0