Sichuan Deyang Haton® hMR60DL Polyphenylene Sulfide, Glass & Mineral Reinforced
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled |
| Manufacturer | Sichuan Deyang Chemical Co. Ltd. |
| Trade Name | Haton® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sichuan Deyang Haton® hMR60DL Polyphenylene Sulfide, Glass & Mineral Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Injection molding, low chlorineInformation provided by Sichuan Deyang Chemical Co., LTD
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.97 g/cc | 0.0712 lb/in³ | GB/T 1033.1-2008 |
| Water Absorption | 0.020 % | 0.020 % | GB/T 1034-2008 |
| Linear Mold Shrinkage, Flow | 0.0018 cm/cm | 0.0018 in/in | GB/T 15585-1995 |
| Linear Mold Shrinkage, Transverse | 0.0062 cm/cm | 0.0062 in/in | GB/T 15585-1995 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 107 | 107 | GB/T 3398.2-2008 |
| Tensile Strength | 167 MPa | 24200 psi | GB/T 1040.2-2006 |
| Elongation at Break | 1.24 % | 1.24 % | GB/T1040.2-2006 |
| Flexural Strength | 235 MPa | 34100 psi | GB/T 9341-2008 |
| Flexural Modulus | 17.5 GPa | 2540 ksi | GB/T 9341-2008 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | GB/T 1843-2008 |
| Izod Impact, Unnotched (ISO) | 47.0 kJ/m² | 22.4 ft-lb/in² | GB/T 1843-2008 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 280 °C | 536 °F | GBT/T 19466.3-2004 |
| Deflection Temperature at 1.8 MPa (264 psi) | 266 °C | 511 °F | GB/T 1634.2-2004 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.80e+16 ohm-cm | 1.80e+16 ohm-cm | GB/T1410-2006 |
| Surface Resistivity per Square | 6.20e+15 ohm | 6.20e+15 ohm | GB/T1410-2006 |
| Dielectric Constant | 4.0 | 4.0 | GB/T 1409-2006 |
| Dielectric Strength | 14.0 kV/mm | 356 kV/in | GB/T1408.1-2006 |
| Dissipation Factor | 0.0010 | 0.0010 | GB/T 1409-2006 |
Users viewing this material also viewed the following:
- Murtfeldt Murylon® A GF Nylon 66, Glass Reinforced
- Nilit FRIANYL A63 CU90 Nylon 6.6 for injection molding, 90% copper filled
- LATI LASTIROL R-V2 Polystyrene (PS) (UL94 V-2) (discontinued **)
- Kraton® G1657 + PP blend + Talc (12/21/67)
- SABIC Innovative Plastics Valox® 310SE0 PBT (Europe-Africa-Middle East)
- Techmer ES Electrafil® J-50/CF/20 Polycarbonate, 20% Carbon Fiber Reinforced
- ChevronTexaco Havoline® TC-W3® Two-Cycle Engine Oil
- Alliance BIS-52 Bonded (Composite) Magnetic Material
- Parker Chomerics CHO-SEAL 1215 Conductive Elastomer
- Lehmann & Voss LUVOCOM® 1105-7825 PEEK, with PTFE
Copyright © lookpolymers.com All Rights Reserved