- Lehmann & Voss LUVOCOM® 1114-8364 PAEK, with carbon fiber, PTFE, lubricant modified
Lehmann & Voss LUVOCOM® 1114-8364 PAEK, with carbon fiber, PTFE, lubricant modified
| Category | Polymer , Thermoplastic , Polyketone , Polyaryletherketone (PAEK), Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1114-8364 PAEK, with carbon fiber, PTFE, lubricant modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Good friction and wear behaviour especially at increased temperatures.Electrically conductive, suitable for continuous discharging of statically generated electricity.Thermic, mechanic and chemical highly stressed parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 190 MPa | 27600 psi | |
| Elongation at Yield | 1.7 % | 1.7 % | |
| 2.2 % | 2.2 % | flexural | |
| Modulus of Elasticity | 18.0 GPa | 2610 ksi | |
| Flexural Strength | 260 MPa | 37700 psi | |
| Flexural Modulus | 15.0 GPa | 2180 ksi | |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | flatwise; ISO 179 1fU |
| 2.50 J/cm² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 5.00 µm/m-°C | 2.78 µin/in-°F | DIN 53752 |
| Maximum Service Temperature, Air | 255 °C | 491 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 305 °C | 581 °F | |
| Vicat Softening Point | 320 °C | 608 °F | DIN ISO 306 |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 10000 ohm | <= 10000 ohm | |
| Insulation Resistance | <= 100000 ohm | <= 100000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 390 °C | 734 °F | mass temp |
| Nozzle Temperature | 390 - 420 °C | 734 - 788 °F | |
| Zone 1 | 370 - 420 °C | 698 - 788 °F | |
| Zone 2 | 380 - 420 °C | 716 - 788 °F | |
| Zone 3 | 390 - 420 °C | 734 - 788 °F | |
| Mold Temperature | 160 - 230 °C | 320 - 446 °F | |
| Drying Temperature | 120 °C @Time 21600 - 36000 sec |
248 °F @Time 6.00 - 10.0 hour |
or |
| 150 °C @Time 14400 - 21600 sec |
302 °F @Time 4.00 - 6.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | dark grey |
Users viewing this material also viewed the following:
- Park Electrochemical Nelcote® F-555 Phenolic Prepreg, NARC/CYDSA Reinforced
- Lehmann & Voss LUVOCOM® 1105-8053/EM/BL PEEK, with glass fiber, easy flowing
- Lucent Polymers 6-01 Nylon 6, General Purpose, Injection Grade
- Latrobe Lescalloy® UT-18 VAC-ARC ; 2.125 in. round High Strength Alloy Steel
- SABIC Innovative Plastics Valox® IQ8280SF PBT+PET
- Teknor Apex MONPRENE® MP 2890M Thermoplastic Elastomer
- Tisan TISLAMID® 6 30% Glass Bead Reinforced Nylon 6
- Topas Advanced Polymers TOPAS® 6013S-04 Cyclic Olefin Copolymer (COC)
- Hexcel® HexPly® M56 180°C (350°F) Out-of-Autoclave Curing Matrix, M56/35%/UD134/AS7-12K
- Haynes 230® alloy, 50% cold reduction
Copyright © lookpolymers.com All Rights Reserved