Sibur 140-13A Compound 8/2 Polyvinyl Chloride (PVC)

Category	Polymer , Thermoplastic , Vinyl (PVC) , PVC, Molded
Manufacturer	Sibur
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Sibur 140-13A Compound 8/2 Polyvinyl Chloride (PVC).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Shall correspond to control sample, approved in accordance with the established procedure. Pores, which can be seen by eyes, are not allowed. Plastic shall no burn at stop of worm extruder for a period of 20 minutes. For insulation of wires and cables operating in intervals of temperatures from -40Â°C to 70Â°C.

Physical Properties	Metric	English	Comments
Density	1.28 - 1.32 g/cc	0.0462 - 0.0477 lb/inÂ³
Water Absorption	<= 0.20 %	<= 0.20 %
Collected Volatile Condensable Material	<= 2.0 %	<= 2.0 %	Loss in mass at 160Â°C during 6 hours

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	>= 19.6 MPa	>= 2840 psi
Elongation at Break	>= 250 %	>= 250 %

Thermal Properties	Metric	English	Comments
Softening Point	170 - 190 Â°C	338 - 374 Â°F
Brittleness Temperature	<= -40.0 Â°C	<= -40.0 Â°F
Flammability Test	<= 15	<= 15	In seconds, method A

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+11 ohm-cm @Temperature 70.0 Â°C	>= 1.00e+11 ohm-cm @Temperature 158 Â°F
	>= 5.00e+13 ohm-cm @Temperature 20.0 Â°C	>= 5.00e+13 ohm-cm @Temperature 68.0 Â°F

Descriptive Properties	Value	Comments
Color	Non-colored, white
Elongation Retained After Ageing	80%	Aged for 7 days at 100Â±2Â°C
Number of Inclusions	<27 psc	With dimensions up to 0.5 mm