Seals Eastern 5403 Nitrile Rubber

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber
Manufacturer Seals Eastern, Inc
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Seals Eastern 5403 Nitrile Rubber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
General purpose NitrileInformation provided by Seals Eastern, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.22 g/cc
1.22 g/cc
ASTM D297, 15
Mechanical Properties Metric English Comments
Hardness, Shore A >= 72
>= 72
ASTM D2240, Type A
78
78
AVG; ASTM D2240, Type A
78

@Temperature 100 °C,
Time 252000 sec
78

@Temperature 212 °F,
Time 70.0 hour
After Dry Heat Aging; ASTM D865
82

@Temperature 100 °C,
Time 605000 sec
82

@Temperature 212 °F,
Time 168 hour
After Dry Heat Aging; ASTM D865
Tensile Strength at Break >= 19.25 MPa
>= 2792 psi
ASTM D412 Method A
22.71 MPa
3294 psi
AVG; ASTM D412 Method A
20.44 MPa

@Temperature 100 °C,
Time 605000 sec
2965 psi

@Temperature 212 °F,
Time 168 hour
ASTM D865
22.94 MPa

@Temperature 100 °C,
Time 252000 sec
3327 psi

@Temperature 212 °F,
Time 70.0 hour
ASTM D865
Tensile Strength, Yield >= 1.49 MPa
>= 216 psi
Stress at Elongation M50; ASTM D412 Method A
1.61 MPa
233 psi
AVG Stress at Elongation M25; ASTM D412 Method A
>= 2.18 MPa
>= 316 psi
Stress at Elongation M100; ASTM D412 Method A
2.30 MPa
334 psi
AVG Stress at Elongation M50; ASTM D412 Method A
4.37 MPa
634 psi
AVG Stress at Elongation M100; ASTM D412 Method A
Elongation at Break 342 %
342 %
AVG; ASTM D412 Method A
283.9 %

@Temperature 100 °C,
Time 605000 sec
283.9 %

@Temperature 212 °F,
Time 168 hour
ASTM D865
307.8 %

@Temperature 100 °C,
Time 252000 sec
307.8 %

@Temperature 212 °F,
Time 70.0 hour
ASTM D865
Modulus of Elasticity 0.01051 GPa
1.525 ksi
ASTM D412 Method A
Shear Modulus 0.00350 GPa
0.508 ksi
ASTM D412 Method A
Secant Modulus 0.009880 GPa
1.433 ksi
ASTM D412 Method A
Tear Strength Test 275
275
(psi); ASTM D624, Die B
Compression Set 8.6 %

@Temperature 100 °C,
Time 79200 sec
8.6 %

@Temperature 212 °F,
Time 22.0 hour
ASTM D395, Test B
14 %

@Temperature 100 °C,
Time 252000 sec
14 %

@Temperature 212 °F,
Time 70.0 hour
ASTM D395, Test B
Thermal Properties Metric English Comments
Glass Transition Temp, Tg -29.4 °C
-21.0 °F
ASTM D1329
Descriptive Properties Value Comments
Strain Energy / Unit Volume at 20% Elongation (psi) 26