Seals Eastern 5053 Ethylene-Propylene Rubber
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Seals Eastern, Inc |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Seals Eastern 5053 Ethylene-Propylene Rubber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General service EPDM.Information provided by Seals Eastern, Inc.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | >= 63 | >= 63 | ASTM D2240, Type A |
| 73 | 73 | AVG; ASTM D2240, Type A | |
| Tensile Strength at Break | >= 8.522 MPa | >= 1236 psi | ASTM D412 Method A |
| 14.73 MPa | 2136 psi | AVG; ASTM D412 Method A | |
| Tensile Strength, Yield | 1.22 MPa | 177 psi | AVG Stress at Elongation M25; ASTM D412 Method A |
| >= 1.36 MPa | >= 197 psi | Stress at Elongation M50; ASTM D412 Method A | |
| 1.73 MPa | 251 psi | AVG Stress at Elongation M50; ASTM D412 Method A | |
| >= 2.25 MPa | >= 326 psi | Stress at Elongation M100; ASTM D412 Method A | |
| 3.21 MPa | 466 psi | AVG Stress at Elongation M100; ASTM D412 Method A | |
| Elongation at Break | >= 191 % | >= 191 % | ASTM D412 Method A |
| 275 % | 275 % | AVG; ASTM D412 Method A | |
| Modulus of Elasticity | 0.01007 GPa | 1.461 ksi | ASTM D412 Method A |
| Shear Modulus | 0.00336 GPa | 0.487 ksi | ASTM D412 Method A |
| Secant Modulus | 0.009473 GPa | 1.374 ksi | ASTM D412 Method A |
| Tear Strength Test | 116 | 116 | (psi); ASTM D624, Die B |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Glass Transition Temp, Tg | -65.0 °C | -85.0 °F | ASTM D1329 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Strain Energy / Unit Volume at 20% Elongation (psi) | 21 |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylex® P1010FRMA Polycarbonate
- Solvay Specialty Polymers Ixef® 1025 Polyarylamide (PARA), 50% Glass Fiber
- Techmer ES HiFill® PA6/6 GF33 NAT001 Y 33% Glass Filled (Dry)
- A. Schulman POLYBATCH™ Blue 4021 Concentrate Based in Polyethylene
- Zeon Chemicals Zetpol® 2030L Hydrogenated Nitrile Elastomomer
- CoorsTek Zirconia-Toughened Alumina, ZTA
- Asahi Kasei Thermylene® P-40FG-0860 40% Glass Fiber Reinforced
- SABIC Innovative Plastics GELOY CR7500 ASA
Copyright © lookpolymers.com All Rights Reserved